Wet welding with covered electrodes (Shielded Metal Arc Welding – SMAW) is the most commonly used method of carrying out welding repair works in a water environment. Limited visibility and the inability to move freely under water result in an increased risk of formation of welding imperfections such as lack of fusion, lack of penetration and arc strikes. The work focused on changes in the properties and structure of steel subjected to the impact of short (0.2 s) arc ignitions generated by covered electrodes in air and under water for three high strength steel grades: S460N, S460M and S500MC. Visual tests, macroscopic and microscopic metallographic tests, microhardness measurements and diffusible hydrogen content in deposited metal determination were performed. A significant influence of the environment on changes in the morphology and microhardness of steel in the vicinity of arc strikes was found. The microhardness of the areas covered by the rapid thermal cycle caused by SMAW increased from 200–230 HV0.5 to 400–500 HV0.5 depending on the steel grade. The presence of welding imperfections: cavities and cracks were detected. The susceptibility of all steel grades subjected to short thermal cycles to cracking was confirmed by the results of measurements of the diffusible hydrogen content: 38.6 ml/100 g and 84.5 ml/100 g for air and water environment, respectively. No influence of changes in the welding current on the behavior of the material in the tested conditions was found. The conducted research shows that leaving arc strikes on the structure may have serious consequences and cause a failure.
Citations
-
9
CrossRef
-
0
Web of Science
-
9
Scopus
Authors (6)
-
Przemysław Raczko
- S.N.SINEMA, Opata Hackiego Street 8-10, 81-213 Gdynia, Poland
Cite as
Full text
- Publication version
- Accepted or Published Version
- DOI:
- Digital Object Identifier (open in new tab) 10.12913/22998624/166061
- License
-
open in new tab
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
Advances in Science and Technology Research Journal
no. 17,
pages 160 - 169,
ISSN: 2080-4075 - Language:
- English
- Publication year:
- 2023
- Bibliographic description:
- Fydrych D., Raczko P., Świerczyńska A., Landowski M., Wolski A., Rogalski G.: Effect of Arc Strikes on High Strength Low Alloy Steels Welded by SMAW// Advances in Science and Technology Research Journal -,iss. 3 (2023), s.160-169
- DOI:
- Digital Object Identifier (open in new tab) 10.12913/22998624/166061
- Sources of funding:
-
- Statutory activity/subsidy
- Verified by:
- Gdańsk University of Technology
seen 99 times
Recommended for you
Weldability of S500MC Steel in Underwater Conditions
- D. Fydrych,
- J. Łabanowski,
- G. Rogalski
- + 5 authors