One of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper an experimental...

The article presents the results of a literature survey and preliminary tests which set out effects of welding conditions on the amount of diffusible hydrogen in deposited metal. Experiments were conducted by using rutile coated electrodes which generate high contents of diffusible hydrogen in deposited metal. The amount of diffusible hydrogen was determined by a glycerin test.Eleven factors were considered: the electrode angle,...

The article describes manufacturing technology of multilayer joints in terms of control the diffusible hydrogen content. Diffusible hydrogen content in deposited metal for multilayer welded joints made of covered rutile electrodes or covered cellulosic and basic electrodes was determined. It was found that after four beads, the diffusible hydrogen content decreases in the case of the first technology from 36 ml/100 g to 18 ml/100...

W artykule przedstawiono szczegółową charakterystykę procedury oznaczania ilości wodoru dyfundującego metodą rtęciową na tle innych metod badawczych i aktualnego stanu wiedzy dotyczącego rozpatrywanego zagadnienia. Omówiono klasyfikację wodoru występującego w złączu spawanym oraz metody oznaczania ilości wodoru dyfundującego w stopiwie ze zwróceniem szczególnej uwagi na metodę rtęciową jako metodę podstawową. Zestawiono zależności...