Thermal behavior of VO2/V2O3 nanostructures obtained at 1000°C under argon atmosphere

Description

The DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 1000°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.

Thermogravimetric analysis (TG) and Differential scanning calorimetry (DSC) measurements were carried out under synthetic air atmosphere from 30°C to 700°C (with a heating rate of 15 °C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum (MS). The gases that come out from the samples during heating were monitored by the quadruple mass spectrometer Netzsch QMS 403C Aeolos. The mass spectra were measured for selected m/z from 12 to 46.

Dataset file

Xero1000Ar.zip

54.8 kB, S3 ETag c1121badb8d492743d4c4c5ca842ace8-1, downloads: 60

The file hash is calculated from the formula
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.

Example script for calculation:
https://github.com/antespi/s3md5

download

File details

License:: open in new tab

CC BY

Attribution
Raw data:: Data contained in dataset was not processed.

Details

Year of publication:

2021

Verification date:

2021-07-14

Dataset language:

English

Fields of science:

materials engineering (Engineering and Technology)

DOI:

10.34808/pagp-m765

Series:

Vanadium oxides

Verified by:

Gdańsk University of Technology

Keywords

References

publication The influence of thermal conditions on V2O5 nanostructures prepared by sol-gel method

Cite as

Authors

seen 118 times

Search