Search
Abstract
This paper presents investigation of cavitation erosion resistance of nitrided austenitic stainless steel X5CrNi18-10. The diffusion layers were produced by using different parameters of atmosphere (N2:H2). The microstructure, chemical composition and phase identification of the modified layer were examined using scanning electron microscopy, glow-discharge optical emission spectrometer and X-ray diffractometry, respectively. Cavitation erosion resistance of produced surface layers was investigated in a rotating disc facility. As a property characterizing the cavitation erosion resistance of manufactured surface layers were proposed incubation period and mass loss after 330 min of cavitation test. It was found that cavitation erosion resistance of modified surface layers is lower than reference material (not treated X5CrNi18-10 stainless steel).
Authors (3)
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Published in:
-
Solid State Phenomena
no. 183,
pages 201 - 206,
ISSN: 1012-0394 - Language:
- English
- Publication year:
- 2012
- Bibliographic description:
- Szkodo M., Sitko A., Gazda M.: Cavitation Erosion Resistance of Austenitic Stainless Steel after Glow-Discharge Nitriding Process// Solid State Phenomena. -Vol. 183., (2012), s.201-206
- Verified by:
- Gdańsk University of Technology
seen 130 times
Recommended for you
Effect of annealing temperature on slurry erosion resistance of ferritic X10CrAlSi18 steel
- M. Buszko,
- A. Krella,
- A. Marchewicz
- + 1 authors