This paper presents investigation of cavitation erosion resistance of nitrided austenitic stainless steel X5CrNi18-10. The diffusion layers were produced by using different parameters of atmosphere (N2:H2). The microstructure, chemical composition and phase identification of the modified layer were examined using scanning electron microscopy, glow-discharge optical emission spectrometer and X-ray diffractometry, respectively. Cavitation erosion resistance of produced surface layers was investigated in a rotating disc facility. As a property characterizing the cavitation erosion resistance of manufactured surface layers were proposed incubation period and mass loss after 330 min of cavitation test. It was found that cavitation erosion resistance of modified surface layers is lower than reference material (not treated X5CrNi18-10 stainless steel).
Autorzy (3)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Solid State Phenomena
nr 183,
strony 201 - 206,
ISSN: 1012-0394 - Język:
- angielski
- Rok wydania:
- 2012
- Opis bibliograficzny:
- Szkodo M., Sitko A., Gazda M.: Cavitation Erosion Resistance of Austenitic Stainless Steel after Glow-Discharge Nitriding Process// Solid State Phenomena. -Vol. 183., (2012), s.201-206
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 130 razy
Publikacje, które mogą cię zainteresować
Effect of annealing temperature on slurry erosion resistance of ferritic X10CrAlSi18 steel
- M. Buszko,
- A. Krella,
- A. Marchewicz
- + 1 autorów