Abstract
Mechanical resistance of Al2O3 + TiO2 nanocomposite ceramic coating deposited by electrostatic spray deposition method onto X10CrAlSi18 steel to thermal and slurry tests was investigated. The coating was produced from colloidal suspension of TiO2 nanoparticles dispersed in 3 wt% solution of Al2(NO3)3, as Al2O3 precursor, in ethanol. TiO2 nanoparticles of two sizes, 15 nm and 32 nm, were used in the experiments. After deposition, coatings were annealed at various temperatures, 300, 1000 and 1200 °C, and next exposed to cyclic thermal and slurry tests. Regardless of annealing temperature and the size of TiO2 nanoparticles, the outer layer of all coatings was porous. The first five thermal cycles caused a rapid increase of aluminum content of the surface layer to 30–37 wt%, but further increase in the number of thermal cycles did not affect the aluminum content. The oxidation rate of coating-substrate system was lower during the thermal tests than during annealing. The oxidation rate was also lower for smaller TiO2 particles (15 nm) forming the coating than for the larger ones (32 nm). The protective properties of Al2O3 + TiO2 coating against intense oxidation of substrate were lost at 1200 °C. Slurry tests showed that coatings annealed at 1000 °C had the best slurry resistance, but thermal tests had weakened this slurry resistance, mainly due to decreasing adhesion of the coating.
Citations
-
1 1
CrossRef
-
0
Web of Science
-
1 3
Scopus
Authors (5)
-
Alicja Krella
-
Andrzej Krupa
-
Arkadiusz Sobczyk
-
Anatol Jaworek
Cite as
Full text
full text is not available in portal
Keywords
Details
- Category:
- Articles
- Type:
- artykuł w czasopiśmie wyróżnionym w JCR
- Published in:
-
CERAMICS INTERNATIONAL
no. 43,
pages 1 - 12,
ISSN: 0272-8842 - Language:
- English
- Publication year:
- 2017
- Bibliographic description:
- Krella A., Krupa A., Gazda M., Sobczyk A., Jaworek A.: Protective properties of Al2O3 + TiO2 coating produced by the electrostatic spray deposition method// CERAMICS INTERNATIONAL. -Vol. 43, (2017), s.1-12
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.ceramint.2017.06.070
- Verified by:
- Gdańsk University of Technology
seen 96 times
Recommended for you
Fatigue Bending of V-Notched Cold-Sprayed FeCoCrNiMn Coatings
- P. Cavaliere,
- A. Perrone,
- A. Silvello
- + 3 authors
Effect of annealing temperature on slurry erosion resistance of ferritic X10CrAlSi18 steel
- M. Buszko,
- A. Krella,
- A. Marchewicz
- + 1 authors