Ball on disk test AL(rf.)-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 not treated (reference).
-
Ball on disk test AL(rf.)-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 not treated (reference).
-
Ball on disk test AT4_11-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT4_11).
-
Ball on disk test AT3_21-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT3_21).
-
Ball on disk test AW4_1-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 WC powder injected (AW4_1).
-
Ball on disk test AT4_4-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 TiN powder injected (AT4_4).
-
Ball on disk test AW4_11-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 WC powder injected (AW4_11).
-
Ball on disk test AT4_1-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 TiN powder injected (AT4_1).
-
Ball on disk test AT4_41-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 TiN powder injected (AT4_41).
-
Ball on disk test AT3_2-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 TiN powder injected (AT3_2).
-
Ball on disk test AW4_4-Al2O3-r15
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 15 mm. Disk material: Al6061 WC powder injected (AW4_4).
-
Ball on disk test AW4_41-Al2O3-r25
Open Research DataHard particle reinforced Al6061 alloy testing. Laser remelting and kinetic injection of particulate material. Ball on disc tribological test. Ball material: Al2O3. Ball diameter: 5 mm. Sliding path radius: 25 mm. Disk material: Al6061 WC powder injected (AW4_41).
-
Cyclic voltammetry curves for FTO/PANI:WO3 nanocomposite
Open Research DataThis dataset contains the results of kinetic electrochemical studies, carried out with cyclic voltammetry (CV) of FTO/PANI:WO3 nanocomposite at various scan rates: 10, 20, 50, 75, 100 and 200 mV/s. The electrolyte was 1M H2SO4 solution. The measurements were performed in a three electrode setup, and with Ag|AgCl|3M KCl as the reference electrode and...
-
Pigment production and secretion by psychrotolerant yeast-like fungi at 25 °C for 2 days
Open Research DataThree strains, named Red, Pink and Black, were grown in five different media with the following compositions: 1% peptone K, 2% glucose; 2% peptone K, 2% glucose; 1% yeast extract, 2% glucose; 1% peptone K, 1% yeast extract, 2% glucose; 1% peptone K, 2% yeast extract, 2% glucose (YPD) for 2 days at 25°C with shaking 180 rpm. The cultures were then centrifuged...
-
Pigment production and secretion by psychrotolerant yeast-like fungi at 15 °C for 4 days
Open Research DataThree strains, named Red, Pink and Black, were grown in five different media with the following compositions: 1% peptone K, 2% glucose; 2% peptone K, 2% glucose; 1% yeast extract, 2% glucose; 1% peptone K, 1% yeast extract, 2% glucose; 1% peptone K, 2% yeast extract, 2% glucose (YPD) for 4 days at 15°C with shaking 180 rpm. The cultures were then centrifuged...
-
Pigment production and secretion by psychrotolerant yeast-like fungi at 20 °C for 2 days
Open Research DataThree strains, named Red, Pink and Black, were grown in five different media with the following compositions: 1% peptone K, 2% glucose; 2% peptone K, 2% glucose; 1% yeast extract, 2% glucose; 1% peptone K, 1% yeast extract, 2% glucose; 1% peptone K, 2% yeast extract, 2% glucose (YPD) for 2 days at 20°C with shaking 180 rpm. The cultures were then centrifuged...
-
Pigment production and secretion by psychrotolerant yeast-like fungi at 15 °C for 2 days
Open Research DataThree strains, named Red, Pink and Black, were grown in five different media with the following compositions: 1% peptone K, 2% glucose; 2% peptone K, 2% glucose; 1% yeast extract, 2% glucose; 1% peptone K, 1% yeast extract, 2% glucose; 1% peptone K, 2% yeast extract, 2% glucose (YPD) for 2 days at 15°C with shaking 180 rpm. The cultures were then centrifuged...
-
Ocean mixed layer dynamics: high-resolution simulations of wind, wave and convective effects
Open Research DataThis dataset contains results of high-resolution numerical simulations of the ocean mixed layer (OML) forced by wind, waves and cooling from the atmosphere, i.e., under strongly turbulent, convective conditions. The goal is to provide detailed, three-dimensional information about OML circulation, turbulent kinetic energy, and temperature and salinity...
-
The spontaneous electron emission and rotational predissociation lifetimes of the diatomic silver anion
Open Research DataThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...
-
Non-adiabatic coupling elements between the diatomic silver anion and neutral silver dimer plus continuum electron
Open Research DataThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...