Opinion about causes of framing of Kingston chest (box cooler) damage, on PSV vessel VS4411 DF-PSV (B-855)
PublicationThe subject of analysis is a damage of welded connection of box cooler framing segments, made as separate bars 50mm thickness, connected by the welds in corners. Studies of documents delivered by Customer shows cracks on the fusion of filet welds and twisting of box cooler frame. The subject of analysis is a damage of welded connection of box cooler framing segments, made as separate bars 50mm thickness, connected by the welds...
-
Weldability of high strength steels in wet welding conditions
PublicationIn this paper are characterized problems of high strength steel weldability in underwater wet welding conditions. Water as a welding environment intensifies action of unfavourable factors which influence susceptibility to cold cracking of welded steel joints. The susceptibility to cold cracking of S355J2G3 steel and S500M steel in wet conditions was experimentally estimated (by using Tekken test). It was concluded that the steels...
-
Calculations of notch stress factor of a thin-walled spreader bracket fillet weld with the use of a local stress approach
PublicationPresence of geometric notches in welded joints causes concentration of strains and stresses, therefore reducing fatigue strength of such joints. This article presents an analysis of stress concentrations in a fillet weld of a spreader mounting bracket on a small sailing yacht. The aim of this article is to direct the attention of designers, manufacturers and regulatory bodies to issues of fatigue cracks that form in brackets fastening...
-
Underwater in situ local heat treatment by additional stitches for improving the weldability of steel
PublicationIn this paper the influence of in situ local heat treatment performed by additional stitches on the weldability of high-strength low-alloy (HSLA) S355J2C+N steel was tested. The investigated steel is characterized by high susceptibility to cold cracking. It is necessary to find a method to improve the quality of welded joints. The local heat treatment was applied as an eect of bead-on plate welding made on the face of a Tekken...
-
Opracowanie technologii naprawy nieciągłości metalicznych w połączeniach spawanych, w konstrukcji podpór przednich pras filtracyjnych położonych na terenie Grupowej Oczyszczalni Ścieków Dębogórze
PublicationCelem niniejszej pracy jest opracowanie wytycznych technologicznych, których wdrożenie pozwoli na usunięcie istniejących pęknięć, co przyczyni się do stabilizacji wymiarowej podpór oraz całej konstrukcji pras. Osiągniecie tego celu wymaga podjęcia następujących działań: - ocenę stanu technicznego naprawianego komponentu- podpór przednich trzech pras filtracyjnych, - określenie własności spawalniczych materiału naprawianego, -...
-
Advantages of the Application of the Temper Bead Welding Technique During Wet Welding
PublicationThermo-mechanically rolled S460ML steel was chosen for welding in underwater wet welding conditions by covered electrodes. The main aim of this study was to check the weldability for fillet welds in a water environment by controlled thermal severity (CTS) tests and to check the influence of temper bead welding (TBW) on the weldability of the investigated steel. Non-destructive and destructive tests showed that S460ML steel has...
-
Designate CTOD Heat Affected Zone of butt weld, Report No: WOiO/II/76/2013
PublicationTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability...
-
CTOD designation for WM and HAZ in butt joint made from S460 ML steel, Expertise No. WOiO/II/82/2015
PublicationTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability to...
-
Designate of CTOD for WM and HAZ, report no: WOiO/II/122/2014
PublicationTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability to...