Rok 2024
-
Direct reduction of pellets through hydrogen: Experimental and model behaviour
PublikacjaThis paper presents the hydrogen reduction behaviour of industrial pellets designed for the efficient hydrogen based direct reduction. The pellets were provided with very low non ferrous oxides percentage (0.52 of basicity index) and with the absence on TiO2 oxides. The pellets measured diameters in the range 1.14–1.72 cm and were characterized in terms of porosity, pores size, tortuosity and compression strength. The pellets were...
-
Hydrogen direct reduction and reoxidation behaviour of high-grade pellets
PublikacjaHigh grade pellets with basicity index close to 0.5 were directly reduced in pure hydrogen atmosphere. The reduction experiments were performed in the temperature range 800 e1000 C at the pressure of 8 bar. The pellets internal structure was analysed through micro tomography observations in the unreduced and reduced conditions. After reduction, the pellets showed a variation of porosity up to more than 15% with a remarkable change...
Rok 2023
-
Comparison of Cu1.3Mn1.7O4 spinels doped with Ni or Fe and synthesized via wet chemistry and solid-state reaction methods, designed as potential coating materials for metallic interconnects
PublikacjaThe influence of the method applied to synthesize Cu-Mn-O spinel was evaluated. The methods selected for the investigation were EDTA gel processes and solid-state reaction synthesis. From the obtained powders, sinters were prepared and assessed in terms of their properties as potential coating materials. Additionally, the influence of Ni and Fe dopants was evaluated. The results show that the EDTA gel processes method seems to...
-
High-temperature Corrosion of ~ 30 Pct Porous FeCr Stainless Steels in Air: Long-Term Evaluation Up to Breakaway
PublikacjaIn this work, a long-term (up to 6000 hours) corrosion evaluation of three porous (~ 30 pct of initial porosity) ferritic iron-chromium alloys with different Cr contents (20, 22, and 27 wt pct of Cr) was carried out at 600 C, 700 C, 800 C, and 900 C in air. Mass gain measurements and SEM analyses revealed that at temperatures above 600 C, all alloys exhibit breakaway corrosion, whereas at 600 C, none of the alloys were heavily...
Rok 2022
-
Effect of Processing Parameters on Strength and Corrosion Resistance of Friction Stir-Welded AA6082
PublikacjaThe friction stir welding method is increasingly attracting interest in the railway sector due to its environmental friendliness, low cost, and ease of producing high-quality joints. Using aluminum alloys reduces the weight of structures, increasing their payload and reducing fuel consumption and running costs. The following paper presents studies on the microstructure, strength, and corrosion resistance of AA6082 aluminum alloy...
-
Glass-ceramic joining of Fe22Cr porous alloy to Crofer22APU: interfacial issues and mechanical properties
PublikacjaThis work deals with the joining of porous Fe22Cr ferritic stainless steel to a dense Crofer22APU plate by using a silica-based, Ba-containing glass-ceramic. The chemical and interfacial stability and the mechanical properties of the joints were evaluated before and after thermal ageing at 700 ◦C for 500hrs. The sintering behaviour of the glass was assessed by using heating stage microscopy (HSM) to study the influence of a porous...
-
Morphology changes in Fe-Cr porous alloys upon high-temperature oxidation quantified by X-ray tomographic microscopy
PublikacjaThe effect of high-temperature oxidation at 850 C (10 h, 30 h, 100 h) and 900 C (10 h) on porous (30 % porosity) ferritic stainless steel (Fe22Cr) has been investigated using synchrotron tomographic microscopy, which allowed for visualisation, separation and quantitative analysis of the metallic core, closed pores, open pores and oxide scale phase. The same regions within the samples were investigated before and after oxidation...
Rok 2021
-
Glass-ceramic sealants and steel interconnects: accelerated interfacial stability and reactivity tests at high temperature
PublikacjaHigh-temperature reactions between glass-ceramic sealants and Fe-Cr alloy interconnects may lead to the formation of undesirable phases, and consequently degradation of solid oxide fuel/electrolyser devices. In this work, three different glass-ceramic sealants (Na-containing, Ba-containing, Sr-containing compositions) and Fe22Cr stainless steel powders (raw and pre-oxidised) are considered in order to test their chemical reactivity...
-
High temperature corrosion evaluation and lifetime prediction of porous Fe22Cr stainless steel in air in temperature range 700–900 °C
PublikacjaThis work describes a high temperature corrosion kinetics study of ~30% porous Fe22Cr alloys. The surface area of the alloy (~0.02 m2 g-1) has been determined by tomographic microscopy. The weight gain of the alloys was studied by isothermal thermogravimetry in the air for 100 hours at 700 - 900 °C. Breakaway oxidation was observed after oxidation at 850 °C (~100 hours) and 900 °C (~30 hours). The lifetime prediction shows the...
Rok 2020
-
Evolution of Ag nanostructures created from thin films: UV–vis absorption and its theoretical predictions
PublikacjaAg-based plasmonic nanostructures were manufactured by thermal annealing of thin metallic films. Structure and morphology were studied using scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM) and X-ray photoelectron spectroscopy (XPS). SEM images show that the formation of nanostructures is influenced by the initial layer thickness as well as the...