seria: Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending liczba: 4
rozwiń zwiń-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-006)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-Con)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-004)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-002)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Measurements of ultrasonic bulk and guided wave propagation in additively manufactured cubes and plates obtained by ultrasonic pulse velocity analyzer and scanning laser vibrometry
Dane BadawczeThe DataSet contains the results of measurements of ultrasonic wave propagation in additively manufactured samples made of polylactic acid (PLA). Three types of raster angles in two consecutive layers were assumed: 0°/90° (#1), 45°/-45° (#2) and 90°/90° (#3) with respect to the x-axis. For each printing variants a cubic sample (#C1-3) with dimensions...
-
Wave propagation signals in concrete beams under 3-point bending
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beams with dimensions 40 x 40 x 160 cm3under the 3-point bending. The beams were made of concrete with the following ingredients: CEM I 42.5R (450 kg/m3), water (177 kg/m3), sand 0-2 (675 kg/m3) and gravel 2-8 (675 kg/m3). The bending test was performed using a Zwick/Roell Z10...
-
Measurements of guided wave propagation in CFRP/steel adhesive joints obtained by scanning laser vibrometry
Dane BadawczeThe DataSet contains guided wave signals measured in adhesive joints of steel plates (steel of type S355 with a thickness of 11.9 mm ) and carbon fibre reinforced polymer (CarboDur S1012 with a thickness of 1.24 mm). The samples were as follows: #0 – intact; #1 – 10% disbond; #2 – 20% disbond; #3 – 50% disbond; #4 – 80% disbond; #5 – 100% disbond.
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #4)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #3)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #2)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #1)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation and digital image correlation measurements of steel bars under 3-point bending
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a bar under a 3-point bending test. The bar was made of steel and had a cross-section of 5.96 × 5.96 mm2 and a length of 200 mm. The three-point bending test was performed using a Zwick/Roell Z10 universal testing machine (UTM), with a distance between supports of 12 cm. The parameters...