Analysis of Residual Stresses and Dislocation Density of AA6082 Butt Welds Produced by Friction Sir Welding

Aleksandra Mirowska; Marek Szkodo; Pasquale Cavaliere; Dorota Moszczyńska; Jarosław Mizera

doi:10.1007/s11661-022-06862-4

Analysis of Residual Stresses and Dislocation Density of AA6082 Butt Welds Produced by Friction Sir Welding

Abstrakt

The Friction Stir Welding (FSW) method was employed to join AA6082 sheets. The welds were produced with different tool traverse speed (200 and 250 mm/min), rotational speed (1000 and 1250 RPM) and tool tilt angle (0 and 2 deg). Based on the analysis of XRD patterns, the total precipitation volume fractions in the nugget zones and the base material were calculated. The FSW process resulted in a reduction in the fraction of precipitates up to 64 pct compared to the parent material. Based on the Williamson–Hall analysis and indentation tests, the residual stresses were calculated. The highest tensile residual stresses of 89.09 ± 6.19 MPa were observed for the base material, and the welding process reduced the residual stresses. The calculated dislocation density in the parent material AA6082 was equal to 8.225 9 1013 m2 , while in the welds a decrease was observed up to the value of 1.419 9 1013 m2. In addition, the FSW process changed the nature of dislocations with edge-type dislocations dominating, while screw dominating character of dislocations were prevalent in the parent material. The mobility of dislocations in the studied welds was higher and reached the value of 16.78 9 10–7m/s, while the dislocation mobility in the parent material was equal to 3.19 9 10–7 m/s. Process parameters during welding have a crucial effect on the amount of heat and strains introduced during the process, and thus influence the residual stresses, dislocation density and mobility, which might have a fundamental impact on the properties of the produced welds.

Cytowania

5

CrossRef
0

Web of Science
5

Scopus

Autorzy (5)

Aleksandra Mirowska (dawniej: Aleksandra Laska) dr inż.
Marek Szkodo dr hab. inż.
Pasquale Cavaliere
- Department of Innovation Engineering, University of Salento, Via Per Arnesano, 73100, Lecce, Italy
Dorota Moszczyńska
- Faculty of Materials Science and Engineering, Warsaw University of Technology, Woloska 141, 02-507, Warsaw, Poland
Jarosław Mizera
- Faculty of Materials Science and Engineering, Warsaw University of Technology, Woloska 141, 02-507, Warsaw, Poland

Cytuj jako

Pełna treść

pobierz publikację

pobrano 96 razy

Wersja publikacji: Accepted albo Published Version
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s11661-022-06862-4
Licencja: otwiera się w nowej karcie

pełna treść artykułu zobacz w serwisie zewnętrznym otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:

Publikacja w czasopiśmie

Typ:

artykuły w czasopismach

Opublikowano w:

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE nr 54, strony 211 - 225,
ISSN: 1073-5623

Język:

angielski

Rok wydania:

2023

Opis bibliograficzny:

Laska A., Szkodo M., Cavaliere P., Moszczyńska D., Mizera J.: Analysis of Residual Stresses and Dislocation Density of AA6082 Butt Welds Produced by Friction Sir Welding// METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE -, (2022),

DOI: