Diamond-Phase (Sp3-C) Rich Boron-Doped Carbon Nanowalls (Sp2-C): A Physico-Chemical And Electrochemical Properties
Abstrakt
The growth of B-CNW with different boron doping levels controlled by the [B]/[C] ratio in plasma, and the influence of boron on the obtained material’s structure, surface morphology, electrical properties and electrochemical parameters, such as -ΔE and k°, were investigated. The fabricated boron-doped carbon nanowalls exhibit activity towards ferricyanide redox couple, reaching the peak separation value of only 85 mV. The flatband potential and the concentration of boron carriers were estimated in the B-CNW samples using the Mott-Schottky relationship. It was shown that the vertically oriented carbon planes are characterized by p-type conductivity and very high hole-acceptor concentration (3.33×1023 cm-3 for a highly doped sample), which provides high electrical conductivity. The enhanced electrochemical performance of B-CNWs electrodes is an advantageous feature that can be applied in ultrasensitive detection or energy storage devices.
Cytowania
-
6 0
CrossRef
-
0
Web of Science
-
6 0
Scopus
Autorzy (10)
-
Miroslaw Sawczak
-
Sanju Gupta
-
Sara Carrizosa
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1021/acs.jpcc.7b06365
- Licencja
- Copyright (2017 American Chemical Society)
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
Journal of Physical Chemistry C
nr 121,
strony 20821 - 20833,
ISSN: 1932-7447 - Język:
- angielski
- Rok wydania:
- 2017
- Opis bibliograficzny:
- Sobaszek M., Siuzdak K., Ryl J., Sawczak M., Gupta S., Carrizosa S., Ficek M., Dec B., Darowicki K., Bogdanowicz R.: Diamond-Phase (Sp3-C) Rich Boron-Doped Carbon Nanowalls (Sp2-C): A Physico-Chemical And Electrochemical Properties// Journal of Physical Chemistry C. -Vol. 121, iss. 38 (2017), s.20821-20833
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1021/acs.jpcc.7b06365
- Weryfikacja:
- Politechnika Gdańska
Powiązane datasety
wyświetlono 228 razy