Effect of process parameters on properties of Mn1.5CuFe0.5O4 spinel oxide coatings deposited by spray pyrolysis method
Abstrakt
One of the critical issues in the lifetime of metallic interconnects is related to their high oxidation rate and Cr diffusion, which negatively affect their performance. In the present study, a novel Fe modified Mn–Cu spinel oxide with the chemical composition of Mn1.5CuFe0.5O4 as protective coating was deposited on the surface of Crofer 22 APU and alumina by the spray pyrolysis method. The effects of different deposition conditions including deposition temperature, spraying speed, and volume of precursor on the properties of deposited spinel coatings were investigated. Scanning electron microscopy characterizations showed that the deposited layer was uniform and non-cracked at the deposition temperature of 400 °C. However, at temperatures of 300 and lower, the deposited layers became non-uniform and cracked. Additionally, spraying with speeds of 10 ml/h and lower resulted in uniform and non-cracked coatings, and a higher spraying speed of 15 ml/h caused a nonuniform and cracked layer. Atomic force microscopy measurements proposed that the value of Ra was reduced by increasing the deposition temperature and reducing the spraying speed. X-ray diffraction characterization showed that deposition temperature has affected the phase structure of deposited spinel oxides on both substrates. According to electrical conductivity measurements, deposited layers at higher deposition temperatures with lower spraying speeds showed higher electrical conductivity and lower activation energy. Decreasing the deposition temperature reduced the electrical conductivity of the spinel oxide coatings.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (4)
-
Federico Smeacetto Prof
- Polytechnic di Torino
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ijhydene.2025.04.355
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
nr 130,
strony 213 - 229,
ISSN: 0360-3199 - Język:
- angielski
- Rok wydania:
- 2025
- Opis bibliograficzny:
- Mehdizade M., Smeacetto F., Winiarski M., Molin S.: Effect of process parameters on properties of Mn1.5CuFe0.5O4 spinel oxide coatings deposited by spray pyrolysis method// INTERNATIONAL JOURNAL OF HYDROGEN ENERGY -, (2025), s.213-229
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ijhydene.2025.04.355
- Źródła finansowania:
-
- National Science Centre (NCN) Opus project number 2023/49/B/ST8/03265 2) National Science Centre (NCN) Opus project number 2023/49/B/ST11/01298
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 0 razy
Publikacje, które mogą cię zainteresować
Fe-modified Mn2CuO4 spinel oxides: coatings based on abundant elements for solid oxide cell interconnects
- J. Ignaczak,
- L. Zeng,
- D. F. Sanchez
- + 6 autorów
Multilayer coatings based on cerium oxide and manganese cobaltite spinel for Crofer22APU SOC interconnects
- E. Zanchi,
- J. Ignaczak,
- G. Cempura
- + 3 autorów