Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
XRD patterns of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon atmosphere.
-
XRD patterns of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (5-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon atmosphere.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C dependent on film thickness
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (2-3 AsP layers) were deposited on a silicon substrate and were annealing at 1000°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films were deposited on a silicon and quartz glass substrate and were annealing at 1000°C under an argon atmosphere.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon...
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Dane BadawczeThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
Powder x-ray diffraction pattern of polycrystalline synthetic leningradite, PbCu3V2O8Cl2
Dane BadawczePolycrystalline sample of Cu2+ (S=1/2) antiferromagnetic PbCu3V2O8Cl2 (synthetic analogue of the mineral leningradite) was prepared by solid state reaction of PbCl2, CuO, and V2O5.
-
Powder x-ray diffraction pattern of polycrystalline Cu(IO3)2*xH2O
Dane BadawczeHydrated copper(II) iodate sample was prepared in water solution by reacting copper(II) sulfate and potassium iodate, following the method described by Peterson (J. Chem. Educ. 1957, 34, 12, 612). The sample was subsequently dried at various temperatures in order to produce an anhydrous Cu(IO3)2:
-
Electrical measurements of the dewetting of metal thin films
Dane BadawczeIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
Sol-gel derived TeO2:RE powders
Dane BadawczeTellurium dioxide powders doped by Europium or Dysprosium were prepared by sol-gel method. Samples were annealed in ix of Ar and O2 atomosphere at 600 degrees. Presence of rare earth dopants and Te4+ phase was confirmed by X-Ray Photoemission Spectroscopy method (XPS). For XPS measurements samples with 1 atomic % and 5 atomic % of dopand were selected.
-
XPS study of the NH4-VOx powders
Dane BadawczeVanadium pentoxide samples were prepared by sol-gel method. The starting solution was prepared by mixing vanadium (V) oxytripropoxide (Aldrich) in an anhydrous ethanol as solvent and acetylacetone. By drying the sol at 323 K for 48 h, it transforms via gel into a xerogel powder. Next, the precursor powder was pressed into the disk-shaped pellets. Samples...
-
Hydrogenation process ofTiO2/BiVO4/PEDOT:PSS observed by XPS method
Dane BadawczeTitania nanotubes synthesis was based on a two-stage anodization process at water/ethylene glycol (5%/95%) electrolyte containing 0.27 M NH4F and 1 M H3PO4 described previously. Anodization process was performed in two-electrode cell compartment using platinum mesh as a cathode. The distance between electrodes was about 2 cm. The anodization voltage...
-
Chemical investigations of the MoO3 doped by K films deposited FTO
Dane BadawczeMoO3 thin films were synthesized via thermal annealing of thin, metallic Mo films deposited onto the FTO substrate using a magnetron sputtering system. The influence of photointercalation of alkali metal cation (K+) into the MoO3 structure on the photoelectrochemical properties of the molybdenum trioxide films was investigated. The chemical characterisation...
-
Depth chemical profile in a CeIr3 sample
Dane BadawczeThe polycrystalline sample of CeIr3 used in the present studies was synthesized by arc-melting cerium (4N) and iridium (3N5) in an arc furnace on a water-cooled copper hearth using a tungsten electrode under a high purity argon atmosphere. A piece of zirconium was used as an oxygen getter. First, a button of Ir was prepared by arc-melting the iridium...
-
XPS investigations of tge tin/tin oxides - CNT composites
Dane BadawczeThe composite of tin/tin oxide nanoparticles with graphene oxide and CMC based on laser ablation technique as an electrode material for energy storage devices were manufactured. The material exhibited a three-dimensional conducting graphene oxide network decorated with tin or tin oxide nanoparticles. The presence of tin/tin oxide in composites was...
-
SPTNO ceramics measured by XPS method
Dane BadawczeSPTNO (Sr-Pr-Ti-Ni-O) ceramic were manufactured by solid state reaction, from oxides compounds. Synthesis conducted in air atmosphere at temperature in a range of 800-900 deg. Chemical composition of prepared materials were measured by XPS (X-Ray photoemision spectroscopy) method. UHV OmicronNanotechnology system with 128 channel Argus hemispherical...
-
SEM inwestigation of the silver nanostructures
Dane BadawczeSilver thin films with a thickness of 1nm, 3nm, 5nm, 7nm and 9nm were deposited by a table-top magnetron sputtering unit in a pure argon plasma from a high-purity silver target. Silicon wafers was used as a substrates. As-deposired films were annealed in Ar atmosphere at 550 Celsius degree for 15 minutes.As a result of annealing, Ag nanostructures formed...
-
Luminescence and FTIR measurements of B2O3-Bi2O3-SrF2 glass and glass-ceramics doped with Eu3+ ions
Dane BadawczeLuminescence and FTIR measurements of B2O3-Bi2O3-xSrF2+2Eu (x=10,20) glass and glass-ceramics. The emission and excitation spectra of the samples depend on the composition and annealing time.
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 25xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
FTIR spectra of gas mixtures from the methanation chamber filled with 25-75wt.% NiO-Al2O3
Dane BadawczeThe dataset includes the FTIR spectra collection of the outlet gas mixtures (CO2, CO, CH4) from reactor chamber filled with 25/75 wt.% NiO-Al2O3 catalyst for perfoming methanation reaction. The inlet gas mixture was composed of 3:1 by vol. H2:CO. Spectra were collected using PerkinElmer FTIR every 1 min.
-
FTIR spectra of gas mixtures from the methanation chamber filled with 50-50wt.% NiO-GDC
Dane BadawczeThe dataset includes the FTIR spectra collection of the outlet gas mixtures (CO2, CO, CH4) from reactor chamber filled with 50/50 wt.% NiO-GDC (Gadolinia Doped Ceria 20mol.%Gd2O3) catalyst for perfoming methanation reaction. The inlet gas mixture was composed of 3:1 by vol. H2:CO. Spectra were collected using PerkinElmer FTIR every 1 min.
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The TPR reduction profile of MCO powder
Dane BadawczeThe dataset includes the TPR reduction profiles of MnCo2O4 (MCO) commercial powder. The dataset includes a cycle of reduction under H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min. Degassed at 200C in He for 1 h.
-
FTIR spectra of gas mixtures from the methanation chamber filled with 50-50wt.% NiO-Al2O3
Dane BadawczeThe dataset includes the FTIR spectra collection of the outlet gas mixtures (CO2, CO, CH4) from reactor chamber filled with 50/50 wt.% NiO-Al2O3 catalyst for perfoming methanation reaction. The inlet gas mixture was composed of 3:1 by vol. H2:CO. Spectra were collected using PerkinElmer FTIR every 1 min.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CeO2/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using CeO2/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method - 50xCMC
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 50xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using modified Pechini/EDTA method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using modified Pechini method consisting of CA (citric acid), PEG (propylene glycol) and EDTA. Exact amount of metal nitrates were dissolved in water followed by addition of gelling agents and heated to 100C. Obtained gel was calcined at 600C for 4h. The powder...
-
The XPS spectra of CeO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of CeO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/1%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/1%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using Al2O3/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using AlOOH/1%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using Al2O3/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Al2O3 (TMDAR)/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
BET adsorption-desorption isotherm of CeO2 prepared using Pechini method
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric pure CeO2 prepared using modified Pechini method - citric acid and propylene glycol (2:1)
-
BET adsorption-desorption isotherm of CeO2 pure
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric pure CeO2 (CA-assisted method of synthesis)
-
BET adsorption-desorption isotherm of nano-ZrO2
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric ZrO2 (CA-assisted method of synthesis)
-
BET adsorption-desorption isotherm of nano-MgO
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric MgO (CA-assisted method of synthesis)
-
BET adsorption-desorption isotherm of nano-SrTiO3
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric SrTiO3 (CA-assisted method of synthesis)
-
BET adsorption-desorption isotherm of nano-CeO2
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 (AlfaAesar)
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Fe
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Fe oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Mn
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Mn oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Cu
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Cu oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Ni
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Ni oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.