The results of the nitrogen adsorption/desorption measurements of CPMD and CPMH
Dane BadawczeThe results of the nitrogen adsorption/desorption measurements of CPMD and CPMH. The adsorption/desorption isothermswere carried out at 77 K using a Quantachrome Autosorb-1C-MS instrument. Sample abbreviations (CPMD, CPMH) are in agreement with the markings used in the linked publication.
-
Evaluation of the electrochemical performance of CPMD in ZICs with 3M ZnSO4 electrolyte
Dane BadawczeThese data contain the results of the electrochemical performance measurements of CPMD in ZICs with 3M ZnSO4 electrolyte, incl. CGD (galvanostatic charge-discharge ) curve and cycling stability of CPMD. Sample abbreviations (CPMD) are in agreement with the markings used in the linked publication.
-
CV (cyclic voltammetry) curves of the CPMD sample at different scan rates
Dane BadawczeThese data contain CV curves of CPMD obtained at a scan rate from 1 mV s−1 to 20 mV s−1. Sample abbreviations (CPMD) are in agreement with the markings used in the linked publication.
-
Ex-situ XRD (X-ray Diffraction) results for electrodes under different charge/discharge states
Dane BadawczeEx-situ XRD was employed to analyze the energy storage mechanism of CPMD in ZICs system. The ZICs were firstly charged to 1.8 V from the open circuit voltage (at around 1.3 V), then discharge to 1.0 V and 0.2 V, and finally recharged to 1.0 V and 1.8 V. Sample abbreviations (CPMD) are in agreement with the markings used in the linked publication.
-
SEM (scanning electron microscopy) and TEM (transmission electron microscopy) images of PMD and PMH
Dane BadawczeThese data contains SEM (scanning electron microscopy) and TEM (transmission electron microscopy) images of PMD and PMH. TEM was performed on a FEI Tecnai F30 transmission electron microscope operating at an acceleration voltage of 200 kV. SEM was done with a SEM, XL30ESEM-FEG with an acceleration voltage of 20 KV. Sample abbreviations (PMH, PMD) are...
-
Raman spectra of CPMH and CPMD
Dane BadawczeThese data contains Raman spectra of CPMH and CPMD. Raman scattering was measured with a RenishawmicroRaman spectrometer (785 nm). Sample abbreviations (CPMH, CPMD) are in agreement with the markings used in the linked publication.
-
Isothermal calorimetry data for cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw calorimetric data determined up to 168 h (Tam Air 3 8-channel isothermal calorimeter) of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.
-
Open porosity and oven-dry density of concretes containing magnetite aggregate (M0-M100) mixes
Dane BadawczeRaw data for determination of open porosity and oven-dry densities of concretes containing different amount of magnetite aggregate (M0-M100) mixes. Sample designation is related to the publication associated with dataset.
-
Particle size distribution (laser granulometry) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain raw results of particle size distribution (by volume) of Bi2O3 and Gd2O3 particles determined using a laser diffraction method (Malvern Mastersizer 2000, Worcestershire, UK).
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw mechanical (compressive strength) data of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.
-
X-ray diffraction (XRD) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
X-ray diffraction (XRD) of silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
TG analyses - content of SiO2 and TiO2 in polystyrene
Dane BadawczeTG analyses were performed for polystyrene spheres coating by SiO2 and then coating by SiO2-TiO2. Thermal analyses of polystyrene spheres only were also performed. The content of inorganic remaining was used for calculation the quantity of coating SiO2 and TiO2 in the polystyrene spheres.
-
TG-hydroxyl groups in TiO2-P25
Dane BadawczeTG analyses were performed for powdered TiO2 - commercial P25 sample, which was heat-treated from room temperature to 500 C in the nitrogen atmosphere. Mass loss at lower temperature such as 120 C was related to the physisorbed water, and that one occurring at 500 C to the chemisorbed hydroxyl groups.
-
TiO2-potential zeta in water
Dane BadawczeData contain results from measurements of zeta potential for powdered TiO2 in a diluted aqueous solution. The measurements were performed in Zetasizer Nano ZS analyser.
-
Photocatalytic decomposition of ethylene on the TiO2-polystyrene spheres
Dane BadawczeData contain results from the measurements of the photocatalytic decomposition of ethylene under UV irradiation with using TiO2 coating on the expanded polystyrene spheres (EPS). EPS-SiO2-TiO2 and EPS-TiO2 were used as the photocatalytic beds in the fluidized bed reactor. Both, stationary and fluidized beds were tested. The comparison of ethylene decomposition...
-
SEM - Expanded polystyrene coated by TiO2 or SiO2-TiO2
Dane BadawczeData contain SEM images taken in SEM Hitachi SU8000 with voltage of 5.0 kV. SEM images show expanded plystyrene spheres coated by a thin layer of TiO2 or bilayer SiO2-TiO2.
-
XRD-TiO2 and SiO2
Dane BadawczeData contain results from XRD measurements of amorphous silica and TiO2 of antase and rutile phases. The commercial TiO2 named as P25 produced by Evonik was also analyzed.
-
Analyses of sulphur in TiO2 by XRFS
Dane BadawczeData contain content of sulphur in TiO2 determined by X-ray fluorescence spectroscopy. The results were obtained by using internal pattern.
-
TiO2-TG analyses -OH groups
Dane BadawczeTG analyses of TiO2 were performed under nitrogen flow to monitor desorption of hydroxyl groups. Physisorbed weak-bonded hydroxyl groups were desorbed totally at around 120oC, whereas chemisorbed ones at around 500oC. The mass loss at these temperatures was used as concentration of hydroxyl groups on TiO2 surface. The amount of analysed TiO2 was 10...