X-ray diffractometry results of the SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.50Fe0.50O3-d (STF50) powder after ball milling. The phase composition of the investigated STF50 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.35Fe0.65O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.35Fe0.65O3-d (STF35) powder after ball milling. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.30Fe0.70O3-d (STF70) powder after ball milling. The phase composition of the investigated STF70 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
Exemplary SEM images of polished cross sections of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum mode.
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Dane BadawczeThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.50Fe0.50O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.50Fe0.50O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.30Fe0.70O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.50Fe0.50O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.50Fe0.50O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at different temperatures
Dane BadawczeIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.30Fe0.70O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
SEM images of symmetrical cell interface with SrTi1-xFexO3-d electrodes and CGO-20 substrate sintered at 800 °C
Dane BadawczeThis dataset contains images of polished cross section of symmetrical cell interface with SrTi1-xFexO3-d (x=0.35; 0.50; 0..70) electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum...