The nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold and pure silver nanostructures and with composition of 25%, 50 and 75% Au. The Omicron NanoTechnology spectrometer with a 128-channel collector was used for measurements. XPS studies were performed at room temperature under a ultra-high vacuum conditions, around 10-9 mBar. The photoelectrons were excited by an Mg-Kα X-Ray source. The X-ray anode was operated at 15 keV and 300 W. The Omicron Argus hemispherical electron analyser with a round aperture of 4 mm was used for the analysis of the emitted photoelectrons. The binding energies were corrected using the background C1s line (285.0 eV). XPS spectra were analysed with Casa-XPS software using Shirley background subtraction and Gaussian–Lorentzian curve as the fitting algorithm.
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
- Oprogramowanie:
- origin
Informacje szczegółowe
- Rok publikacji:
- 2021
- Data zatwierdzenia:
- 2021-07-26
- Data wytworzenia:
- 2020
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/6k7q-w061 otwiera się w nowej karcie
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Cytuj jako
Autorzy
wyświetlono 112 razy