Chemical diffusion coefficient of oxygen (D*) of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95 and 1.00) at different temperatures

Opis

In this dataset are presented D* values designated based on the electrical conductivity relaxation (ECR) mesurement of the SrxTi0.30Fe0.70O3 (x=0.90, 0.95, 1.00) materials. The applied temperatures were 800 °C, 750 °C, 700 °C, 650 °C, and 600 °C. Studies were performed in a small tube furnace (internal diameter ~20 mm) with 64 cm³ gas volume. During the four-point single frequency electrochemical impedance spectroscopy measurement (1 Hz), the oxygen partial pressures were changed from 20% O₂ to 10% O₂ and the reverse.

D* was designated for both cases incorporation and removal of oxygen.

Plik z danymi badawczymi

D vs temp.xlsx

8.8 kB, S3 ETag 90e1d26416228931ca90aecd3395c9b3-1, pobrań: 3

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa

Informacje szczegółowe

Rok publikacji:

2022

Data zatwierdzenia:

2024-11-27

Język danych badawczych:

angielski

Dyscypliny:

Automatyka, elektronika i elektrotechnika (Dziedzina nauk inżynieryjno-technicznych)
inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/9bbn-ar91

Finansowanie:

Badanie oraz minimalizacja ohmowych i polaryzacyjnych strat w tlenkowych ogniwach elektrochemicznych przez zastosowanie nanokrystalicznych warstw ceramicznych

Seria:

Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 30 razy

Wyszukiwarka