Comparisson of area specific resistance of the SrTi1-xFexO3-d porous oxygen electrodes and state-of-the-art LSCF sintered at optimal conditions

Opis

In this dataset are presented results of the polarization resistance of optimaly sintered SrTi1-xFexO3-d porous oxygen electrodes in symetrical cell (1000 °C; 800 °C and 800°C respectively x = 0.35; 0.50 and 0.70). For commparison were selected commercially avilable state-of-the-art LSCF (Europa) sintered at 1050 °C. The measurement temperature range was between 800 °C and 500 °C in syntetic air (40 ml min-1 flow). Results converted to electrode surfaces area and dived by two electrodes.

Plik z danymi badawczymi

best_ASR_STFx_arhenius_vs_LSCF.xlsx

8.7 kB, S3 ETag d5968587fbef0785acd73e7dd504bf12-1, pobrań: 42

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY-NC-SA

Użycie niekomercyjne - Na tych samych warunkach

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-05-23

Data wytworzenia:

2019

Język danych badawczych:

angielski

Dyscypliny:

Automatyka, elektronika i elektrotechnika (Dziedzina nauk inżynieryjno-technicznych)
inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI: