Formation of gold anostructures detected by SEM microscope

Opis

Gold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2  of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%). The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness of the films was  measured in situ by a quartz crystal microbalance. To analyze the surface morphology of the samples, a FEI Quanta FEG 250 scanning electron microscope (SEM) operated at 10 kV was used. Samples with 1.2, 1.5 and 3.4 nm of initial Au layer anealed at 550 deg for 5, 10 and 15 minutes were measured.

Plik z danymi badawczymi

550.zip
39.0 MB, S3 ETag 4c52864f5394e836a9ad66a0c1e323bb-1, pobrań: 61
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
pobierz plik 550.zip

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:
2021
Data zatwierdzenia:
2021-07-26
Data wytworzenia:
2021
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/xbns-wn33 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 118 razy