Raman spectra were recorded at room temperature using a micro-Raman spectrometer (Invia, Renishaw) equipped with an edge filter with different excitation wavelengths and lasers: UV λ = 325 nm (HeCd), blue λ = 488 nm (Ar+), green λ = 514 nm (Ar+), and IR λ = 785 nm (IR diode) and 50× microscope objective. To avoid sample heating, the radiation power was set below 2 mW while the laser spot diameter on the sample surface was about 2 µm. The spectral resolution was better than 2 cm−1. Each sample was analyzed at five randomly selected points and each spectrum was averaged from five measurements.
The BDD@D and BDD@H were synthesized in the Microwave Plasma Assisted Chemical Vapor Deposition process. Diamond films were deposited on p-type (100) silicon substrates (1 × 1 cm2) and studied by Raman spectroscopy.
The selected measurements were utilized when preparing the manuscript published in Small DOI: 10.1002/smll.202208265
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2023
- Data zatwierdzenia:
- 2024-02-05
- Data wytworzenia:
- 2023
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- automatyka, elektronika, elektrotechnika i technologie kosmiczne (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/80jy-zk15 otwiera się w nowej karcie
- Finansowanie:
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Cytuj jako
Autorzy
Wersja ten dokument posiada różne wersje
-
Aktualna wersjawersja 1.0Data publikacji wersji 2024-02-05
wyświetlono 132 razy