Surface modifcation of PMMA polymer detected by XPS

Opis

In order to obtain the experimental specimens, four PMMA/PC61BM samples with the following  mass proportions were prepared: 10%, 20%, 30%, and 40%. In addition, as a reference, a PMMA sample without  PC61BM was prepared as well. For the fabrication process, PC61BM 99.5% (Solenne BV), chloroform HPLC  (Sigma Aldrich), and PMMA (commercially available sheets) were used. Firstly, the PMMA was dissolved in  chloroform. Next, the obtained solution was divided into vials, approx. 1 ml each. Ten PC61BM was added to  the vials and sonifcated for 20 min. Finally, a dispersion of the PC61BM in the PMMA was spin-cast on a clear  glass substrate at 1500 rpm for 25 s. Te probe liquids for water contact angle measurement were distilled water  from a local supplier. Argon of purity of≥99.998 (% vol.), used as the plasma forming gas, was purchased from  Air Liquide Polska. 

The detailed chemical composition of samples was analyzed by X-ray photoemission spectroscopy (XPS). XPS measurement was carried out using Omicron NanoScience equipment. Samples were measured at room temperature, under the ultra-high vacuum conditions and pressures below 1.1 x 10-8 mBar. The photoelectrons were excited by a Mg-Kα x-ray source operated at 15 keV and 300 W. Argus hemispherical spectrophotometer equipped with 128 channel detector was used for photoelectrons energy measurements. The data analysis was performed with the CASA XPS software, using Shirley background subtraction and Gauss-Lorentz curve fitting algorithm by the least-squares method - GL (30).

Plik z danymi badawczymi

xps.zip
288.9 kB, S3 ETag 968f5cbfe77c26da2458483922c53d55-1, pobrań: 35
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
pobierz plik xps.zip

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:
origin, casa XPS

Informacje szczegółowe

Rok publikacji:
2021
Data zatwierdzenia:
2021-07-26
Data wytworzenia:
2021
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/ajzf-5x63 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 93 razy