Tellurite based glass doped by Eu3+ ions - XPS measurements

Opis

Eu³⁺ doped tellurite glass ceramics containing SrF₂ nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF₂ nanocrystals in glass matrices after annealing at 370 °C. FTIR studies revealed absorption bands in the range of 500–850 cm⁻¹ characteristic to TeO₂ glasses. Obtained materials exhibited emission originated from the ⁵D_J (J = 0–2) to the ⁷F_J (J = 0–4) transitions of Eu³⁺ ions under 395 and 465 nm excitations. TRES measurements indicated presence of two different surroundings of the Eu³⁺ ions. In glass ceramics samples longer lifetimes of 615 nm emission of Eu³⁺ were achieved in comparison to the precursor glass.

Plik z danymi badawczymi

glass.zip

1.3 MB, S3 ETag 60ae39e75f77085e49796f41f843069a-1, pobrań: 31

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: origin

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-06-24

Data wytworzenia:

2016

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/pppn-tj17

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

Marcin Stanisław Łapiński dr hab. inż.
Instytut Nanotechnologii i Inżynierii Materiałowej
numer orcid 0000-0002-3283-2886otwiera się w nowej karcie
Twórca

wyświetlono 86 razy

Wyszukiwarka