Temperature of formation of Au nanostructures

Opis

Nanostructures were obtained via annealing of thin Au films. In order to determine possible nanoislands formation mechanisms, dependence on initial film thickness was examined. For the surface morphology studies, nanograin structure and chemical composition analysis, SEM, HR TEM and EDS measurements were performed, respectively. Morphology studies shown that, the temperature at which nanostructures form varies for different substrates, which indicates high impact of the substrate material on the nanostructures formation. In the case of silicon substrate, besides the phenomenon of spinodal dewetting, the effect of eutectics on the nanostructures was additionally taken into consideration.

Plik z danymi badawczymi

Au pp.zip

26.7 MB, S3 ETag 6994ed97676a558e9e83e0870059f75e-1, pobrań: 66

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY-NC-ND

Użycie niekomercyjne - Bez utworów zależnych
Oprogramowanie:: origin

Informacje szczegółowe

Rok publikacji:

2019

Data zatwierdzenia:

2021-05-14

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

https://doi.org/10.1007/s11468-019-01021-9

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 128 razy

Wyszukiwarka