XRD diffraction patterns for strontium ferrite molybdate-based compounds: as-prepared, reduced and reoxidized

Opis

The dataset contains the XRD diffractograms collected at room temperature for SFM, LSFM and SFMNb in 3 different oxidation states, namely: as-prepared, reduced and reoxidized.

The powders were synthesized by the Pechini method from nitrates mostly (chloride for Nb precursor, and ammonium molybdate for Mo). The obtained gel was calcined at 1100 deg. C for 10 h, then material was ground and underwent XRD analysis on BRUKER D2 PHASER XE-T operating with Cu-KAlpha radiation. Then the powders were reduced in the flow of pure hydrogen. The reductive atmosphere were kept from the RT until the end of the reduction. The reduction temperature was 800 deg. C with the 4h of hold at peak temperature. After reduction, XRD measurements were repeated. Lastly, the reduced powders were reoxidized in air for 4 h at 800 deg. C. Reoxidized samples were analyzed by XRD. 

The dataset contains 3 respective folders. Files in them are both *.raw format, which can be opened e.g.  by HighScore, and also the one exported to *.asc, which don't require additional proffesional software.

Plik z danymi badawczymi

XRD_SFM_LaNb_asprepared_reduced_reoxidized.zip
411.5 kB, S3 ETag da607573a811903fb57be65739a68a0c-1, pobrań: 4
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Embargo na plik:
2025-06-15
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:
HighScore, XRD software

Informacje szczegółowe

Rok publikacji:
2024
Data zatwierdzenia:
2024-01-15
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/fasb-cy80 otwiera się w nowej karcie
Finansowanie:
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

wyświetlono 55 razy