Wyniki wyszukiwania dla: MICROEMULSIONS
-
FTIR spectra of Ce0.9M0.1O2 synthesised by reverse microemulsion method
Dane BadawczeThe dataset consist of the FTIR spectra of Ce0.9M0.1O2 synthesised by reverse microemulsion method, after calcination at 500 degrees.
-
The XPS spectra of Ce0.8Ni0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Ni0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XPS spectra of Ce0.8Cu0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Cu0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XRD diffraction patterns of Ce0.9M0.1O2 prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution using tetramethylammonium hydroxide (TMAOH). After the precipitation, the sediment was centrifuged and rinsed with alcohol several times. Precursors powder...
-
The XRD diffraction patterns of annealed Ce0.9M0.1O2 powders prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution of nitrates using TMAOH. The sediment was cetrifuged and rinsed with alcohol several times. Powders were dried and calcinated at 500 degrees for 2 h, followed...
-
The XAS spectra of O-K edges, M-L edges and Ce-M edges in Ce0.9M0.1O2
Dane BadawczeThe dataset consists of XAS spectra of O-K edges, M-L edges of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) synthesised by reverse microemulsion method. XAS spectra were collected at PIRX beamline in SOLARIS National Synchrotron Radiation Centre. Measurements were perfomed under ultra high vacuum in total electron yield (TEY) mode.
-
The TPR reduction profile of Ce0.9M0.1O2
Dane BadawczeThe dataset includes the TPR reduction profiles of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared by the reverse microemulsion method. After the synthesis powders were dried, then calcined at 500 degrees for 2 h. The measurements were carried out in H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min.
-
The XRD diffraction patterns of Ce(Pr,Sm)O2-s samples
Dane BadawczeThe dataset includes XRD diffraction patterns of Ce(Pr,Sm)O2-s samples of various stoichiometries of Pr and Sm dopants. Samples were produced using aqueous soft chemistry methods (microemulsion method).
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.15Sm0.05O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.15Sm0.05O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.2O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.2O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Sm0.2O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Sm0.2O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.1Sm0.1O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.1Sm0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.05Sm0.15O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.05Sm0.15O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Fe0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Fe0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Co0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Co0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Mn0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Mn0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Ni0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Ni0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with CeO2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with CeO2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Cu0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Cu0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The changes of outlet gases concentrations from SOFC with Ce(Pr,Sm)O2-s layers
Dane BadawczeThe dataset includes The changes of outlet gases concentrations from SOFC with Ce(Pr,Sm)O2-s layers. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.9Cu0.1O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.9Cu0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of SOFC with Ce0.9Co0.1O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.9Co0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of SOFC with Ce0.8Co0.1Cu0.1O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Co0.1Cu0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of SOFC with Ce0.8Co0.15Cu0.05O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Co0.15Cu0.05O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.