Search
Open Research Data
We will help you in:
- creating metadata for the dataset
- selecting the appropriate licenses
- preparing data for sharing
- adding a new version of the dataset
- grouping of datasets in a collection
Benefits:
All data is stored on PG servers and is backed up
Data can be quoted and tracked with individual DOI
Update data whenever you want without losing access to old version numbers
Create collections and add thematically related datasets to them
Associate data with people, publications and projects indexed on the platform
Present the contents of the set or how the data was created graphically
Create a dataset and get DOI without publishing your data
High standards of data preservation confirmed by CoreTrustSeal certificate for trustworthy repositories
Contact at: open-data@pg.edu.pl
Filters
total: 24619
filtered: 20
Show data from Digital Pathology
Open Research Data
-
H2-TPR and O2-TPD results for Sr1.05Ti0.30Fe0.70O3-d materials
Open Research DataThis dataset contains results of H2-TPR (temperature programmed reduction) and O2-TPD (temperature programmed desorption) measuremnt fot Sr1.05Ti0.30Fe0.70O3-d material. Experiment was performed using an apparatus equipped with a TCD detector (Buck Scientific, USA), cold trap, and heated gas transfer line. The profiles were collected using the PeakSimple...
-
H2-TPR and O2-TPD results for Sr1.00Ti0.30Fe0.70O3-d materials
Open Research DataThis dataset contains results of H2-TPR (temperature programmed reduction) and O2-TPD (temperature programmed desorption) measuremnt fot Sr1.00Ti0.30Fe0.70O3-d material. Experiment was performed using an apparatus equipped with a TCD detector (Buck Scientific, USA), cold trap, and heated gas transfer line. The profiles were collected using the PeakSimple...
-
H2-TPR and O2-TPD results for Sr0.90Ti0.30Fe0.70O3-d materials
Open Research DataThis dataset contains results of H2-TPR (temperature programmed reduction) and O2-TPD (temperature programmed desorption) measuremnt fot Sr0.90Ti0.30Fe0.70O3-d material. Experiment was performed using an apparatus equipped with a TCD detector (Buck Scientific, USA), cold trap, and heated gas transfer line. The profiles were collected using the PeakSimple...
-
H2-TPR and O2-TPD results for Sr0.95Ti0.30Fe0.70O3-d materials
Open Research DataThis dataset contains results of H2-TPR (temperature programmed reduction) and O2-TPD (temperature programmed desorption) measuremnt fot Sr0.95Ti0.30Fe0.70O3-d material. Experiment was performed using an apparatus equipped with a TCD detector (Buck Scientific, USA), cold trap, and heated gas transfer line. The profiles were collected using the PeakSimple...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for SrxTi0.30Fe0.70O3-d cathode sintered at 900 °C measured at 700 °C
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with SrxTi0.30Fe0.70O3-d (x=0.90, 0.95, 1.00 and 1.05) cathodes sintered at 900 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Results converted to electrode surfaces area and dived by...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for SrxTi0.30Fe0.70O3-d cathode sintered at 800 °C measured at 700 °C
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with SrxTi0.30Fe0.70O3-d (x=0.90, 0.95, 1.00 and 1.05) cathodes sintered at 800 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Results converted to electrode surfaces area and dived by...
-
Particle size distributions (PSD) and the specific surface area (BET) results for SrxTi0.30Fe0.70O3-d materials
Open Research DataThis dataset contains results of particle size distributions (PSD) and BET measuremnt fot SrxTi0.30Fe0.70O3-d materials (x=0.90, 0.95, 1.00 and 1.05). The PSD of the powders were obtained using a Zetasizer Nano dynamic light scattering analyser (Malvern Panalytica). Measurements of the STF70-x solution in ethanol using backscattering mode .
-
The electrical conductivity relaxation curve of the SrxTi0.30Fe0.70O3 (x=0.90 and 1.00) at 700 °C
Open Research DataIn this dataset are presented exemplary curves used for analysis of the electrical conductivity relaxation (ECR) mesurement of the SrxTi0.30Fe0.70O3 (x=0.90, 1.00) materials. The applied measuring temperature were 700 °C. Studies were performed in a small tube furnace (internal diameter ~20 mm) with 64 cm3 gas volume. During the four-point single frequency...
-
Dilatometry results of SrxTi0.30Fe0.70O3-d materials
Open Research DataThis dataset contains results of dilatometry measurements of SrxTi0.30Fe0.70O3-d (x=0.90, 0.95, 1.00 and 1.05) materials. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrxTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for...
-
Thermogravimetric analysis (TGA) of the SrxTi0.30Fe0.70O3-d materials
Open Research DataThis dataset contains results of thermogravimetric analysis (TGA) fot SrxTi0.30Fe0.70O3-d materials (x=0.90, 0.95, 1.00 and 1.05). The TGA experiments were carried out using a microbalance (CI Precision MK5) in the temperature range between 900 °C and 200 °C. During the whole measurement procedure, air was fed to the furnace chamber at a flow rate of...
-
X-ray diffractometry results of the Sr1.05Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.05Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr1.00Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.00Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr0.95Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.95Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr0.90Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.90Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrodes sintered at 1050 °C before and after test
Open Research DataThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrode sintered at 1050 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using...
-
SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C before and after test
Open Research DataThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrode sintered at 800 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using a FEI...
-
SEM images of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...