The present paper is aimed at determining the less investigated effects of hydrogen uptake on the microstructure and the mechanical behavior of the oxidized Zircaloy-2 alloy. The specimens were oxidized and charged with hydrogen. The different oxidation temperatures and cathodic current densities were applied. The scanning electron microscopy, X-ray electron diffraction spectroscopy, hydrogen absorption assessment, tensile, and...

The effect of cathodic polarization conditions on hydrogen degradation of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints, obtained using flux cored arc and submerged arc welding methods, was evaluated. Slow strain rate tensile tests of base material and welded specimens, ferrite content measurements, scanning electron microscopy observations, and statistical analysis were performed. It was found that hydrogenation...

Depleting fossil fuel resources and anthropogenic climate changes are the reasons for the intensive development of new, sustainable technologies based on renewable energy sources. One of the most promising strategies is the utilization of hydrogen as an energy vector. However, the limiting issue for large-scale commercialization of hydrogen technologies is a safe, efficient, and economical method of gas storage. In industrial practice,...

The influence of hydrogen on a (Co0⋅2Cu0⋅2Mg0⋅2Ni0⋅2Zn0.2)O HEO with a rock salt structure was studied. Two forms of this HEO (nanopowder and sinter) were prepared via mechanochemical synthesis (MS) and additional heat treatment, respectively. The chemical stability of the synthesized samples in a pure hydrogen atmosphere was investigated using Sievert’s technique. High-pressure hydrogenation at 250 ◦C had no noticeable effect...