The influence of Be addition on the structure and thermal properties of alkali-silicate glasses
PublicationBe-Na-(Li)-Si oxide glasses containing up to 15 mol% of BeO were prepared. Their structure was characterized by X-ray powder diffraction and Raman as well as infrared spectroscopic techniques, while their chemical compositions were examined by Inductively Coupled Plasma Optical Emission Spectrometry. All materials were found to be amorphous and contain Al contaminations from minor dissolution of the alumina crucibles. The results...
-
Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Open Research DataLinear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO2, 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O, Li2O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered...
-
Nonlinear impedance in oxide glasses containing single and mixed alkali ions
PublicationThe aim of the present was to find more clues on the nonlinearities in impedance of oxide glasses. The first family of researched glasses has a composition of FeO-P2O5-Na2O. Oxide glasses containing iron and alkali are well known for a very low alkali ion mobility and may be considered purely polaron conducting. These glasses show no detectable nonlinearities in the impedance spectra. The second was a family of ionic conducting...
-
Mixed conductivity in tungstenite-phosphate glasses containing alkali metal ions
PublicationThe conductivity of glasses in the 50WO3-(50-x)P2O5-xA2O (A = Na, K, Cs) system has been investigated as a function of composition. It is shown that in tungstenite-phosphate glasses containing different alkali metal ions the conductivity decreases with an increase in the alkali metal ion content. A decrease in conductivity is larger for heavier ions and reaches more than seven orders of magnitude in the case of glass containing...
-
Photocatalytic performance of alkali metal doped graphitic carbon nitrides and Pd-alkali metal doped graphitic carbon nitride composites
Publication -
Influence of the structure of vanadate-phosphate glasses containing alkali ions on their polaronic properties
PublicationBadano wpływ struktury szkieł wanadanowo-fosforanowych zawierających jony metali alkalicznych na ich właściwości polaronowe metodą NMR.
-
Linear and nonlinear impedance in iron oxide glasses containing alkaline ions and alkali free
PublicationThe linear and nonlinear impedance spectra of oxide glasses were measured in the frequency range of 1 mHz to 1 MHz and in the temperature range of 153K to 483K. Two groups of iron oxide glass samples were prepared, the first one containing alkaline ions and the second one without alkali. In the first group, compositions of glasses were as follows: (in %mol) 50% SiO2 , 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O,...
-
Spectroscopic properties of the Ce-doped borate glasses
Publication -
Luminescent properties of Ln3+ doped tellurite glasses containing AlF3
PublicationThe low-phonon energy tellurite glasses TeO2-BaO-Bi2O3 and TeO2-BaO-Bi2O3-AlF3 triply doped with Eu3+, Tb3+, Tm3+ ions in two different molar ratios were synthesized using melt-quenching technique. Their structure and luminescence properties were widely investigated by X-ray Diffraction (XRD), Differential Scanning Calorimetry (DSC), Fourier Transform Infrared Spectroscopy (FTIR) and Photoluminescence Spectroscopy (PL). The luminescence...
-
Electrical properties of Na2O-CaO-P2O5 glasses doped with SiO2 and Si3N4
PublicationSodium-calcium-phosphate glasses doped with SiO2 or Si3N4 having similar sodium ion concentrations were prepared by melt quenching. The conductivity was measured by impedance spectroscopy under nitrogen atmosphere in a wide frequency range (10 mHz–1 MHz) and wide temperature range (153–473 K). At 36.6 °C, DC conductivities of all glasses vary between 1.1 ∗ 10−12 and 8.9 ∗ 10−12 S cm−1 and have similar activation energies (between...