Search results for: linear impedance
-
Electrochemical cell impedance spectra at Eoc+100mV
Open Research DataThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electrochemical cell impedance spectra at Eoc+200mV
Open Research DataThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electrochemical cell impedance spectra at Eoc-100mV
Open Research DataThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electrochemical cell impedance spectra at Eoc-200mV
Open Research DataThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Carbonized Metal-Organic Frameworks-based strucutres with aluminium, phosphorus and nitrogen
Open Research DataThe dataset includes Raman spectra of carbonized Metal-Organic Frameworks (MOF) [acquired on Renishaw] and electrochemical properties of the materials [acquired on EC Lab], which includes techniques such as Linear Sweep Voltammetry (LCV), Electrochemical Impedance Spectroscopy (EIS), Taffel slope and Chronopotentiometry (CP).
-
Electrochemical data for carbonized metal-organic framworks with cobalt
Open Research DataThe data includes the Metal-Organic Frameworks (MOF) measurements, where cobalt was added. The research focuses on the impact of aluminium on Oxygen Evolution Reaction (OER). The measurements were conducted on [EC Lab]. The techniques included are Linear Sweep Voltammetry (LSV), Tafel slope, Chronopotentiometry (CP) and Electrochemical Impedance Spectroscopy...
-
Dielectric properties of barium-vanadate glasses
Open Research DataThe linear impedance of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Open Research DataElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.