The XRD pattern of CeO2/10wt.%Ni with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor nitrate solution (betacyclodextrin). The dataset includes 5-90 2 theta degree measurement. Nonreduced. Sintered at 400oC for 4h.
-
The XRD pattern of CeO2/10wt.%Mn prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Fe prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Cu prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Ni prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4h in air.
-
The XRD pattern of CeO2/10wt.%Co prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement.
-
The XRD pattern of CeO2/10wt.%Cu prepared without BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Fe prepared without BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Mn prepared without BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The TPO oxidation profile of CeO2/10wt.%Co with BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The XRD pattern of CeO2/10wt.%Co prepared without BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Ni prepared without BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The TPO oxidation profile of CeO2/10wt.%Mn with BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Ni with BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Cu with BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Fe with BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Fe. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Cu with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Mn with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Co with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPO oxidation profile of CeO2/10wt.%Cu without BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Ni with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPO oxidation profile of CeO2/10wt.%Mn without BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Co without BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Ni without BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Fe with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Fe. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Co without BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Ni without BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Cu without BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Mn without BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
XPS measurements of the Fe-Bi based glass
Open Research DataFe-Si-O and Fe-Si-Pb-O glass was measured by XPS method. The influence of Pb dopand on the glass structure, including the valence of iron, was investigated. The influence of the annealing temperature on the behavior of iron in glass was also investigated. Studies have confirmed the mixed valence of iron in glasses and a high proportion of metallic Fe.
-
The luminescence study of Bi-doped Cs2AgInCl6 double perovskite.
Open Research DataHere, we report a halide precursor acid precipitation method to synthesize Cs2AgIn1−xBixCl6 (x = 0, 0.02, 0.04, 0.08, 0.16, 0.32, 0.64, and 1) microcrystals. Cs2AgInCl6 and Bi derivative double perovskites show broadband white light emission via self-trapped excitons (STEs) and have achieved the highest internal quantum efficiency of up to 52.4% at...
-
Sb measurements in a Bi-Sb-Te ceramics materials
Open Research DataThe influence of the temperature of the annealing of ceramic materials with the composition Bi0.5Sb1.5Te3O9 was investigated. The materials were annealed at the temperature of 440 degrees Celsius and 450 degrees Celsius. There were no significant differences in the valence of antimony and other elements.
-
Detection of the Ag nanoparticles in Te-Bi-Ba-Oa glass
Open Research DataThe influence of the manufacturing parameters of tellurium-bismuth-barium glasses on the presence of silver nanoparticles was investigated. Glasses were annealed at 330, 335, 340, 345 and 350 degrees Celsius for 24 and 48 hours. Presence of the Ag nanoparticles was measured by XPS method. The growth of nanoparticles was observed along with the extension...
-
Full CI ground state potential energy curves and one-electron relativistic corrections for hydrogen molecule in various basis sets
Open Research DataThis dataset consists of Full CI ground state Born-Oppenheimer potential energy curves and one-electron relativistic corrections for hydrogen dimer. Nonrelativistic energies, as well as one electron relativistic corrections (treated perturbatively with help of the Cowan-Griffin Hamiltonian) are presented for internuclear distances between 0.8 and 10...
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Cu
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Cu oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Co
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Co oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Mn
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Mn oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Ni
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Ni oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Fe
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Fe oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - full run
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - pre-run (10s)
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Experimental database of 3D lattice structure scaffolds testing
Open Research DataDataset contains results of validation (experimental testing) of 3D lattice scaffolds proposed in the paper "Mathematical approach to design 3D scaffolds for the 3D printable bone implant". There are presented three series of experimental testing for each of seven tested scaffolds: