Polyurethane Glycerolysate as a Modifier of the Properties of Natural Rubber Mixtures and Vulcanizates
PublicationChemical recycling of polyurethanes can be realized in several different ways, but the most important methods are glycolysis and glycerolysis. Both methods permit recovery of polyols (when the process is realized with the mass excess of depolymerizing agent) or substitutes of polyols, which contain urethane moieties in the main chains and terminate mainly in hydroxyl groups (when the process is realized with the mass excess of...
-
Cast polyurethanes obtained from reactive recovered polyol intermediates via crude glycerine decomposition process
PublicationIn this work, the possibility of applying intermediates from polyurethane waste recycling in polyurethane synthesis was presented. Polyurethanes were synthesised in a two-step method using a mixture of petrochemical polyol and glycerolysate, used as a reactive component, 4,4-diphenylmethane diisocyanate (MDI) and 1,4-buthanediol (BD). Glycerolysates were produced during decomposition of polyurethane elastomer by crude glycerine...
-
Thermoplastic polyurethanes with glycolysate intermediates from polyurethane waste recycling
PublicationThe polyol is a major component in polyurethane formulations and therefore introducing to the formulation recycled polyol (obtained during decomposition process) allows decreasing the usage of pure petrochemical components. In this work, thermoplastic polyurethanes were prepared using various mixtures of a petrochemical macrodiol poly(ethylene-butylene adipate)diol (PEBA) and a recycled glycolysate intermediate, called glycolysate...
-
Effect of glycolysate obtained from polyurethane wastes on mechanical properties of rubber materials
PublicationThe paper presents the possibility of utilization of wastes from polyurethane foams. In this work the results of mechanical investigations of materials obtained from natural rubber mixtures with a mixture of glycolysate and biodiesel glycerine as a plasticizer are described. The measurements of mechanical properties showed rather good tensile strength, elongation at break and modules of extensions M100%, M200%, M300% of obtained...
-
The Effect of Polyurethane Glycolysate on the Structure and Properties of Natural Rubber/Carbon Black Composites
PublicationIn this work the use of polyurethane chemical recycling product (i.e. glycolysis of polyurethane waste realized with the mass excess of polymer) as a plasticizer for natural rubber-based composites was proposed. The effect of plasticizer type (napthenic oil and polyurethane foam glycolysate) and amount (2, 4, 6 or 8 parts per 100 parts of natural rubber) on the processing properties of rubber mixtures and chemical structure, swelling,...
-
Thermal degradation behavior of lignin-modified porous styrene-divinylbenzene and styrene-bisphenol A glycerolate diacrylate copolymer microspheres
Publication -
Polyurethane glycolysate from industrial waste recycling to develop low dielectric constant, thermally stable materials suitable for the electronics
PublicationWe are utilizing a new method to improve the dielectric properties of a conventional polymer using a recycled polymer product. The polyurethane foams are recycled by glycolysis process and the derived material was applied to improve the dielectric properties of the brittle DGEBA epoxy resin. Two main parameters that determine the applicability of the material as a dielectric (the dielectric constant and dielectric loss), were studied...
-
Mechanical and thermo-mechanical properties of natural rubber composites filled with submicron- and nano-sized silica particles and prepared using glycolysate as a plasticizer
PublicationThe main aim of this work was to examine the selected mechanical and thermo-mechanical properties of natural rubber/silica composites prepared using glycolysate as a plasticizer. Prepared composites contained different amounts of submicron- (10, 15, 20 or 25 pphr) or nano-particles (0.5, 0.75, 1.0 or 1.25 pphr). The tensile properties, tear resistance, hardness, abrasion resistance and resilience of prepared materials were determined....
-
Synthesis and characterisation of polyurethane elastomers with semi-products obtained from polyurethane recycling
PublicationIn this work polyurethane elastomers were synthesised by using different mixtures of a petrochemical and glycerolysate polyols and 4,4-diphenylmethane diisocyanate (MDI). Glycerolysate polyol was produced from polyurethane foam decomposition using crude glycerine as a decomposition agent. The structure and thermal properties of obtained semi-product were similar to the polyol used in the synthesis of original foam. Glycerolysate...
-
The changes of crosslink density of polyurethanes synthesised with using recycled component. Chemical structure and mechanical properties investigations.
PublicationThis paper aims at the utilisation of glycerolysate (Gly) obtained in polyurethane recycling process by means of crude glycerine, which has in its structure hydroxyl end groups that allow for further processing. Polyurethanes (PUs) were synthesised using prepolymer method with the mixture of neat polyol and glycerolysate, in different ratios, with 4,4-diphenylmethane diisocyanate (MDI). The prepolymer was subsequently extended...
-
Single-phase product obtained via crude glycerine depolymerisation of polyurethane elastomer: structure characterisation and rheological behaviour
PublicationPolyurethane recycling is a topic of growing interest due to the increasing amount of polyurethanewaste. The main purpose of polyurethane feedstock recycling is to recover the starting polyol, a valuable material. In thiswork, amethod of polyurethane thermo-chemical recycling, glycerolysisbymeansof crude glycerine, is proposed. Themaineffort is focusedonthe employment of crude glycerine without purification from biodiesel production...
-
Rheological characteristics of oligomeric semiproducts gained via chemical degradation of polyurethane foam using crude glycerin in the presence of different catalysts
PublicationPolyurethane (PU) recycling is a topic of growing interest due to the increasing amount of polyurethane waste. The main purpose of polyurethane chemical recycling is to recover the starting polyol. In this study, a method of polyurethane thermochemical recycling, glycerolysis by means of crude glycerin, is proposed. This work presents a comparative study of commercial catalysts used in order to accelerate the decomposition process,...
-
Investigation of polyurethane elastomer–steel joints using glass lacquer as an adhesive agent
PublicationThis article describes an innovative method of coupling polyurethane elastomer (based on polyurethane glycolysate) with constructional steel, by implementation of a Glaspur®—glass lacquer containing latent polyurethanes and monosilane adhesion promoters. The commonly applied coupling agent is Cilbond® 45SF glue or its derivatives. Additionally, glycolysate was synthesised from polyurethane waste and 1,3-propylene glycol in 6:1...
-
A comparative study on selective properties of Kraft lignin–natural rubber composites containing different plasticizers
PublicationEffect of plasticizer type on the kraft lignin–nat- ural rubber composite microstructure and selected proper- ties was determined. The composites were prepared with addition of a commonly used naphthenic oil plasticizer to study the decomposition product of polyurethane (glyc- erolysate) and its characteristics. Kraft lignin powder was incorporated into the natural rubber matrix in amounts of 10 and 40 parts per 100 parts of natural...
-
Thermo-Chemical Decomposition Study of Polyurethane Elastomer Through Glycerolysis Route with Using Crude and Refined Glycerine as a Transesterification Agent
PublicationDue to the increasing amount of polyurethane waste, chemical recycling of these materials is a topic of growing interest for many researchers. The primary pur- pose of polyurethane feedstock recycling is to recover the starting polyol. In this study glycerolysis using glycerine from two sources and two purity grades is proposed as a method of chemical recycling. The main effort of this paper focuses on the employment of commercial...
-
Janusz Datta prof. dr hab. inż.
PeopleIn 1988, Janusz Datta finished his studies at the Gdańsk University of Technology (GUT), Faculty of Chemistry. Since then he has been employed at the Faculty of Chemistry in the Department of Polymer Technology. During the first six years of employement he was worked as a scientist. In this period, he travelled extensively to ZACHEM company located in Bydgoszcz to gain practical experience related to chemical processing. In 1994,...
-
Softwood-lignin/natural rubber composites containing novel plasticizing agent: Preparation and characterization
PublicationComposite materials based on natural rubber were obtained by using glycerolysate (decomposition prod- uct of polyurethane) as a novel plasticizer. In order to determine the effect of various lignin content, four different filler amounts were used, namely, 5 phr (parts per 100 parts of natural rubber) of lignin (WLI5G), 10 phr (WLI10G), 20 phr (WLI20G), and 40 phr (WLI40G). The reference specimen without lignin (WLI0G) was also...
-
Modyfikacja kompozytów elastomerowych NR za pomocą ligniny i glicerolizatu
PublicationPrzedmiotem opisanych w niniejszym artykule badań są wulkanizaty kauczuku naturalnego. Celem pracy było zbadanie wpływu ligniny oraz glicerolizatu na wybrane właściwości kompozytów zawierających kauczuk naturalny. Strukturę chemiczną przygotowanych materiałów potwierdzono, wykorzystując analizę spektroskopową w podczerwieni (FTIR). Zbadano również właściwości mechaniczne przy statycznym rozciąganiu, twardość, ścieralność oraz odbojność...
-
Evaluation of the glycerolysis process and valorisation of recovered polyol in polyurethane synthesis
PublicationIn this study, the glycerolysis of polyurethane (PU) foam and the applicability of obtained glycerolysate (GLY) for cast PUs were investigated. It was found that crude glycerine with purity grade of 84% might be successfully used for the glycerolysis. The optimal conditions were determined as follows: reaction time of 60 min at 220 °C using dibutyltin dilaurate catalyst (0.5%). Moreover, the purification of GLY by means of liquid-liquid...
-
The influence of different glycerine purities on chemical recycling process of polyurethane waste and resulting semi‐products
PublicationChemical recycling is the most favourable recycling method due to the possibility of polyol recovery. This work is dedicatedto the utilisation of crude glycerine and polyurethane waste. It aims at determining the impact of the use of glycerine fromthe production of biodiesel with various degrees of purity as a cleavage agent on the decomposition process of polyurethanefoam. The influence of glycerine purit y on the chemical structure...