Rok 2014

• Cross-linking of epoxy-oligomeric mixtures in the presence of modified phenol-formaldehyde resins

  Publikacja

  • M. Bratychak
  • G. Strap
  • P. Bruździak
  • J. T. Haponiuk (dawniej: J. Haponiuk)

  - Ukrainian Chemistry Journal - Rok 2014

  Cross-linking of epoxy oligomeric mixtures consisting of industrial epoxy resin ED-20, oligoetheracrylate TGM-3, peroxide derivative of epoxy resin ED-24 and phenol-formaldehyde oligomer with unsaturated methacrylate fragments or peroxide groups was studied in the presence of polyethylenepolyamine at room temperature and heated to 383, 403 or 423 K for 15, 30, 45, 60 and 75 minute. The influence of mixture composition, temperature...

  Pełny tekst do pobrania w portalu

Rok 2006

• Strukturuvannaa epoksi-oligoesternih sumiščej v prisutnosti peroksidnoï pohidnoï epoksidnoï smoli ED-20

  Publikacja

  • M. Bratyczak
  • T. Czervinskij
  • M. Gagin
  • J. Namieśnik
  • A. Mietlarek-Kropidłowska

  - Ukrainian Chemistry Journal - Rok 2006

  W pracy przedstawiono wyniki badań sieciowania mieszanin epoksyoligoestrów opartych na żywicy epoksydowej ED-20 (w tym modyfikowanej) oraz m.in. na oligoestroakrylanie TGM-3, przy czym jako utwardzacz zastosowano polietylenopoliaminę (PEPA).Usieciowane tworzywa analizowano pod kątem wpływu składu mieszaniny, ilości poszczególnych składników, jak również czasu i temperatury prowadzenia procesu na zawartość frakcji żelowej oraz twardość...

  Pełny tekst do pobrania w serwisie zewnętrznym