Electrical properties of nanostructures in lead-silicate glasses and nanocomposites doped with iron oxide

Opis

Electrical properties of iron oxide nanostructures observed in silicate glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15, 20 and 25 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where x=15 and 20 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573 K and formed into button-shaped samples. Afterwards pellets were annealed at 673K, cooledwith the furnace and polished to the thickness of about 1mm.
Electrical properties were analyzed by electrostatic force microscopy (EFM) NT-MDT Ntegra. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2013.10.008

Plik z danymi badawczymi

set8.zip

140.4 MB, S3 ETag 9071c7c64892ebd9e1a6bdf1ede9af84-1, pobrań: 59

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: Gwyddion

Informacje szczegółowe

Rok publikacji:

2014

Data zatwierdzenia:

2021-05-05

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/1q92-5m88

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Electronic conductivity in the SiO2-PbO-Fe2O3 glass containing magnetic nanostructures

Cytuj jako

Autorzy

wyświetlono 112 razy

Wyszukiwarka