In the dataset, are included SEM images of molybdenum gallium carbide MAX materials.
The MAX materials were synthesised according to the procedure:
1) Gring of Mo2C powder with liquid gallium for 60 min in agate mortar at molar ration equal to Mo2C:Ga=1:10.
2)Transfer to the quartz ampule.
3) Evacuating and purging the ampule in order to remove oxygen. Closing the ampule under vacuum.
4) High-temperature annealing at 850 deg. C for 48 hours. The heating rate was maintained at 10 deg. C per minute.
5) Removing potentially formed oxides through leaching with 35% hydrochloric acid.
6) Drying under vacuum at 50 deg. C to dry mass.
Plik z danymi badawczymi
Mo2Ga2C.zip
17.5 MB,
S3 ETag
318f12b447170831b9935e2414feabcd-1,
pobrań: 61
Hash pliku liczony jest ze wzoru
Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2022
- Data zatwierdzenia:
- 2022-09-20
- Data wytworzenia:
- 2021
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)
- inżynieria chemiczna (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/rnbb-6w53 otwiera się w nowej karcie
- Finansowanie:
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
- dane badawcze SEM images of Ni-Mo2CTx/Mo2Ga2C before and after catalytic dry reforming of methane
- dane badawcze XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials