Stiffness modulus (deformation sweep test) of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)

Opis

Dataset presents data of stifness modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Material was obtained from the field before compaction, and compacted in Road Research Laboratory. Specimen size: f=100 mm, h=60mm.  Specimen before the test were cured for more than 28 days at T of 20C and RH of 40-70%.

Data was obtained in the HYD-25 hydraulic universal machine (Cooper Ltd) for 1 temperature (+20°C). Deformation sweep test was used (on the basis of indirect tensile stiffness modulus test; IT-CY scheme acc. to EN 12697-24 standard)

Test load was selected as impulse loading with varied target deformation range – from 2 µm up to 15 µm.

Plik z danymi badawczymi

Cold recycling - C3E5.5 (Miniatura).xlsx
41.3 kB, S3 ETag 45f81f987ed3acfb26f242aa1c41ba7a-1, pobrań: 0
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa

Informacje szczegółowe

Rok publikacji:
2025
Data zatwierdzenia:
2025-04-18
Język danych badawczych:
angielski
DOI:
Identyfikator DOI 10.34808/nmab-ek34 otwiera się w nowej karcie
Finansowanie:
Seria:
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

Autorzy

wyświetlono 14 razy