The morphology of vanadate glass-ceramics containing BaTiO3 measured with the use of AFM

Opis

The structure of vanadate glass-ceramics doped with BaTiO3 was measured by AFM technique. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573 K) brass plate and pressed by another plate. A subset of as-quenched samples was heat treated in air at the temperature of 633 K (close to the crystallization temperature) for 6 h and cooled with the furnace. The structure has been studied by atomic force microscopy with NT-MDT Ntegra AFM microscope on fresh fractured samples.

Plik z danymi badawczymi

set26.zip

21.1 MB, S3 ETag c1615e21f347714fb379679da7abb91d-1, pobrań: 69

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: Gwyddion

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-05-23

Data wytworzenia:

2013

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/6fat-d958

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Nanostructure and dielectric behavior of vanadate glasses containing BaTiO3

Cytuj jako

Autorzy

wyświetlono 115 razy

Wyszukiwarka