The morphology of vanadate glasses containing BaTiO3 measured with the use of AFM

Opis

The morphology of vanadate glasses doped with BaTiO3 was measured with the use of AFM method. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573 K) brass plate and pressed by another plate. The structure has been studied by atomic force microscopy with NT-MDT Ntegra AFM microscope on fresh fractured samples.

Plik z danymi badawczymi

set25.zip

29.7 MB, S3 ETag 74202338ae15bfa6bedd16e237b35df5-1, pobrań: 69

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:: Gwyddion

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-05-23

Data wytworzenia:

2013

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/w3p6-jw71

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Nanostructure and dielectric behavior of vanadate glasses containing BaTiO3

Cytuj jako

Autorzy

wyświetlono 114 razy

Wyszukiwarka