The structure of lead-silicate glasses containing nanocrystallites of iron oxides

Opis

The structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573 K and formed into button-shaped samples. Afterwards pellets were annealed at 673K, cooled with the furnace. The presence of crystalline phases was examined by the X-ray diffraction method with the use of a Philips X'Pert Pro MPD system with CuKα radiation. Detailed information can be found in: http://dx.doi.org/10.1016/j.ssi.2013.10.008

Plik z danymi badawczymi

set11.zip

45.0 kB, S3 ETag f7d7e415e99605192d57b0ec52626e61-1, pobrań: 55

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2014

Data zatwierdzenia:

2021-05-06

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/r2bc-t337

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Electronic conductivity in the SiO2-PbO-Fe2O3 glass containing magnetic nanostructures

Cytuj jako

Autorzy

wyświetlono 133 razy

Wyszukiwarka