Thermal behavior of TeOx xerogel powder under different atmospheres

Opis

The DataSet contains the results of the thermal behavior of the TeOx xerogel powder measured under different atmospheres. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised to 75°C for the next 2h. The obtained gel was dried at 120°C under an argon atmosphere.

Thermogravimetric analysis (TG) and Differential scanning calorimetry (DSC) measurements were carried out under argon atmosphere from 40°C to 910°C (with a heating rate of 5 °C/min) and under synthetic air atmosphere in the temperature range 40-500°C (with a heating rate of 10 °C/min) using Netzsch STA 449 F1.

Plik z danymi badawczymi

DSC-TG.zip

355.4 kB, S3 ETag 88a0b265403d9a1649e7e21664316443-1, pobrań: 41

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2021

Data zatwierdzenia:

2021-07-14

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/tm6p-gm05

Seria:

TeO2-based materials

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 92 razy

Wyszukiwarka