Topography of barium-vanadate glasses - Open Research Data - MOST Wiedzy

Wyszukiwarka

Topography of barium-vanadate glasses

Opis

The topography of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was performed in porcelain crucibles at 1273 K for 10–30 min, depending on glass composition. The melts were poured on preheated (to 393 K) brass plate and pressed by another plate to obtain flat circular pellets of 1-2 mm thickness and 10-20 mm in diameter.
An Olympus LEXT OLS4000 confocal scanning laser microscope (CSLM, Olympus Life Science, Hambur, Germany ) was used to examine the morphology of as-quenched samples. 3D color images were obtained using a 405 nm laser and photomultiplier detector with the maximum obtained optical magnification of 2160x.

 

Plik z danymi badawczymi

set23.zip
25.7 MB, S3 ETag 9d1baaab7d5ca88321ccb7ed68ed650e-1, pobrań: 13
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
pobierz plik set23.zip

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:
2021
Data zatwierdzenia:
2021-05-24
Data wytworzenia:
2014
Język danych badawczych:
angielski
Dyscypliny:
  • Inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/kdda-pf07 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

wyświetlono 52 razy