Influence of processing conditions on crystal structure of BiNbO 4 ceramics

Abstrakt

Bismuth niobate (BiNbO4) has attracted attention as a low-fired ceramics with promising microwave application potential. It belongs to the bismutocolumbite oxides with similarly to scheelite-like stibiotantalite structure (SbTaO4) A3+B5+O4. Aim of the present research was to fabricate BiNbO4 ceramics by solid state reaction route from the mixture of simple oxides viz. Bi2O3, and Nb2O5, and study its phase composition as well as crystal structure by X-ray diffraction method. The Rietveld refinement method was utilized for analysis of diffraction patterns. It was found that the mass change effects finished at temperature T=500C and the total mass change was about Δm=-0.78%. It was found that BiNbO4 ceramics sintered in ambient air exhibited multiphase composition i.e. apart from the major a-BiNbO4 phase the orthorhombic Bi5Nb3O15, Bi3Nb17O47 and cubic Bi3NbO7 phases were present. An increase in sintering temperature caused an increase in amount of major a-BiNbO4 phase which adopted an orthorhombic symmetry described well by Pnna(52) space group.

Cytowania

  • 0

    CrossRef

  • 3

    Web of Science

  • 2

    Scopus

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
Ciencia & Tecnologia dos Materiais nr 29, strony e215 - e218,
ISSN: 0870-8312
Język:
angielski
Rok wydania:
2017
Opis bibliograficzny:
Lisińska-Czekaj A., Czekaj D., Plewa J.: Influence of processing conditions on crystal structure of BiNbO 4 ceramics// Ciencia & Tecnologia dos Materiais -Vol. 29,iss. 1 (2017), s.e215-e218
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ctmat.2016.03.003
Weryfikacja:
Politechnika Gdańska

wyświetlono 12 razy

Publikacje, które mogą cię zainteresować

Meta Tagi