Abstrakt
The ionic Seebeck coefficient was studied in copper selenide with Cu1.99Se, Cu1.95Se and Cu1.8Se stoichiometry which was synthesized with a melt crystallization method. To measure the ionic Seebeck coefficient of copper ions, 0.15C6H12N4CH3I + 0.85CuI solid-state electrolyte was prepared. Electrolyte layers were pressed with copper selenide powder into a sandwich-like structure. At the temperature of 410 K, the materials have ionic Seebeck coefficient values close to each other, about 1100 μV/K. In the case of β-phase structure (Cu1.8Se material), changes in the measured Seebeck coefficient were observed—with decreasing temperature, the ionic thermopower firstly increased reaching about 1230 μV/K and then decreased to 950 μV/K at 355 K. In the Cu1.99Se material, a phase transition to the α-phase was observed during cooling. The ionic Seebeck coefficient values gradually increased from 1030 to 1220 μV/K at 370 K, when the material is in the low-temperature phase. The measured difference between the ionic thermopower of the two phases well matches calculations based on the entropy of the transition (presence part of the Seebeck coefficient) and different activation energies of ionic transport (transport part).
Cytowania
-
1
CrossRef
-
0
Web of Science
-
1
Scopus
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s10853-023-09107-w
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
JOURNAL OF MATERIALS SCIENCE
nr 58,
strony 17034 - 17044,
ISSN: 0022-2461 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Trawiński B.: Ionic thermoelectric effect in Cu2-δSe during phase transition// JOURNAL OF MATERIALS SCIENCE -Vol. 58, (2023), s.17034-17044
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1007/s10853-023-09107-w
- Źródła finansowania:
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 52 razy