Nanocrystalline Polymer Impregnated [Fe(pz)Pt(CN)4] Thin Films Prepared by Matrix-Assisted Pulsed Laser Evaporation

Abstrakt

In this work, the fabrication of [Fe(pz)Pt(CN)4] (pz = pyrazine) thin films by means of matrix-assisted pulsed laser evaporation (MAPLE) was investigated. As starting material, a cryogenically cooled suspension of anocrystalline [Fe(pz)Pt- (CN)4] (0.35wt.-%) in a mixture of 1,1-dichloroethane and polyethylene glycol (PEG) was used. Films of a thickness up to 150–200 nm were deposited on Si substrates by laser ablation at λ = 1064 nm of the cryogenically cooled material. PEG impregnated films exhibit a cooperative first-order hysteretic spin crossover behavior around 155 K as detected by Raman spectroscopy. Most interestingly, deposition of a crystalline material was achieved through MAPLE deposition

Cytowania

  • 1 3

    CrossRef

  • 0

    Web of Science

  • 1 3

    Scopus

Autorzy (8)

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
EUROPEAN JOURNAL OF INORGANIC CHEMISTRY nr 2019, strony 3249 - 3255,
ISSN: 1434-1948
Język:
angielski
Rok wydania:
2019
Opis bibliograficzny:
Mirosław S., Jendrzejewski R., Maskowicz D., Yann G., Gosh A., Gazda M., Czechowski J., Śliwiński G.: Nanocrystalline Polymer Impregnated [Fe(pz)Pt(CN)4] Thin Films Prepared by Matrix-Assisted Pulsed Laser Evaporation// EUROPEAN JOURNAL OF INORGANIC CHEMISTRY -Vol. 2019,iss. 27 (2019), s.3249-3255
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1002/ejic.201900231
Weryfikacja:
Politechnika Gdańska

wyświetlono 987 razy

Publikacje, które mogą cię zainteresować

Meta Tagi