Wyniki wyszukiwania dla: BISMUTH ANTIMONY TELLURIDE
-
BET specific surface area measurements of bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
BET specific surface area measurements of silica-coated bismuth oxide(Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
BET specific surface area measurements of silica-coated bismuth oxide (Bi2O3)/gadolinium oxide (Gd2O3) core-shell structures
Dane BadawczeThe BET specific surface area was measured using an N2 adsorption/desorption isotherm (Micromeritics ASAP 2460, Norcross, GA, USA).
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Dane BadawczeData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
X-ray diffraction (XRD) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide Bi2O3+Gd2O3 structures
Dane BadawczeExcel (*.xlsx) and Csv (*.csv) files containing raw mechanical (compressive strength) data of cement pastes after 1, 2, 7 and 28 days of curing
-
X-ray diffraction (XRD) of silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
Particle size distribution (laser granulometry) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain raw results of particle size distribution (by volume) of Bi2O3 and Gd2O3 particles determined using a laser diffraction method (Malvern Mastersizer 2000, Worcestershire, UK).
-
X-ray diffraction (XRD) of silica-coated bismuth oxide/gadolinium oxide (Bi2O3+Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw mechanical (compressive strength) data of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.
-
Isothermal calorimetry data for cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw calorimetric data determined up to 168 h (Tam Air 3 8-channel isothermal calorimeter) of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.