Wyniki wyszukiwania dla: CATHODE MATERIALS FOR ION-BATTERIES
-
SEM micrographs of V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 nanorods as cathode materials before and after the galvanostatic charge/discharge curves.
-
SEM micrographs of V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 nanocrystals as cathode materials before and after the galvanostatic charge/discharge curves.
-
Cycling performances of the V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. The...
-
Cycling performances of the V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. ...
-
Cycling performances of the V2O5 nanostructures as cathode material in Na-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanostructures with different morphology obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here...
-
Rate performance of the V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
Rate performance of the V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
Rate performance of (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method under an initial pressure of 50 bar ((NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities in the voltage...
-
Rate performance of mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method without initial pressure (mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities...
-
Cyclic voltammetry curves of the V2O5 nanorods (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanorods obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanorods (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Valence state of Manganium in a MnCoO ceramics
Dane BadawczeManganium -cobalt based ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. In order to determine valence states of the Mn, X-Ray photoemission...
-
Thermal behaviour of NH4VO3 microcasketoids
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microcasketoids under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 nanoflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate nanoflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 elongated microcrystals
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate elongated microcrystals under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass...
-
Thermal behaviour of commercial avaible NH4VO3
Dane BadawczeThe DataSet contains the results of the thermal behavior of the commercially available ammonium metavanadate (CAS 7803-55-6) under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also...
-
Thermal behaviour of NH4VO3 microflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Measurements of radiation emission of a portable power bank with a capacity of 10400 mAh
Dane BadawczeThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell (Fig. 1). The test setup was configured to measure a portable power...
-
Measurements of radiation emission of a portable power bank with a capacity of 5200 mAh
Dane BadawczeThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell. The test setup was configured to measure a portable power bank...
-
Measurements of radiation emission of a portable power bank with a capacity of 2600 mAh
Dane BadawczeThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell. The test setup was configured to measure a portable power bank...