Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-002)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-Con)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-004)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-006)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Measurements of ultrasonic bulk and guided wave propagation in additively manufactured cubes and plates obtained by ultrasonic pulse velocity analyzer and scanning laser vibrometry
Dane BadawczeThe DataSet contains the results of measurements of ultrasonic wave propagation in additively manufactured samples made of polylactic acid (PLA). Three types of raster angles in two consecutive layers were assumed: 0°/90° (#1), 45°/-45° (#2) and 90°/90° (#3) with respect to the x-axis. For each printing variants a cubic sample (#C1-3) with dimensions...