Wyniki wyszukiwania dla: FE3O4/TIO2 NANOCOMPOSITES
-
SEM - Expanded polystyrene coated by TiO2 or SiO2-TiO2
Dane BadawczeData contain SEM images taken in SEM Hitachi SU8000 with voltage of 5.0 kV. SEM images show expanded plystyrene spheres coated by a thin layer of TiO2 or bilayer SiO2-TiO2.
-
Photoluminescence spectra of TiO2
Dane BadawczeThese data contain photoluminescence spectra of TiO2 measured at the temperature of liquid nitrogen. There is a comparison of the photoluminescence spectra of TiO2 heat treated at 400-600oC in the ambient (Ar) and reduced (H2) atmospheres. These emission spectra were recorded after TiO2 excitation with a wavelength of 290 nm
-
XRD-TiO2 and SiO2
Dane BadawczeData contain results from XRD measurements of amorphous silica and TiO2 of antase and rutile phases. The commercial TiO2 named as P25 produced by Evonik was also analyzed.
-
Mercury intrusion porosimetry (MIP) results of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite)
Dane BadawczeMercury intrusion porosimetry (MIP) data - curves of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite) in *.opju (Origin) format.
-
TiO2-TG analyses -OH groups
Dane BadawczeTG analyses of TiO2 were performed under nitrogen flow to monitor desorption of hydroxyl groups. Physisorbed weak-bonded hydroxyl groups were desorbed totally at around 120oC, whereas chemisorbed ones at around 500oC. The mass loss at these temperatures was used as concentration of hydroxyl groups on TiO2 surface. The amount of analysed TiO2 was 10...
-
TiO2-zeta potential
Dane BadawczeData contain results from the measurements of zeta potential of TiO2 versus pH. Data are saved as original files and in the format of Excel file. measurements were perfomed in Zetasizer Nano ZS with using Multi-Purpose Titrator MPT-2.
-
Compressive strength and density of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite)
Dane Badawcze*.ODS - open-data source spreadsheet - Dataset presenting:
-
Analyses of sulphur in TiO2 by XRFS
Dane BadawczeData contain content of sulphur in TiO2 determined by X-ray fluorescence spectroscopy. The results were obtained by using internal pattern.
-
Photocatalytic decomposition of acetaldehyde over TiO2 (titanium dioxide) supported on nickel foam and Ni-doped (nickel-doped) TiO2
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using as photocatalytic systems TiO2 (titanium dioxide) supported on nickel foam, TiO2 supported on oxidized nickel foam and TiO2 doped by metallic nickel (Ni) powder. The detailed equipment and measurement...
-
TiO2-potential zeta in water
Dane BadawczeData contain results from measurements of zeta potential for powdered TiO2 in a diluted aqueous solution. The measurements were performed in Zetasizer Nano ZS analyser.
-
Photocatalytic decomposition of ethylene on the TiO2-polystyrene spheres
Dane BadawczeData contain results from the measurements of the photocatalytic decomposition of ethylene under UV irradiation with using TiO2 coating on the expanded polystyrene spheres (EPS). EPS-SiO2-TiO2 and EPS-TiO2 were used as the photocatalytic beds in the fluidized bed reactor. Both, stationary and fluidized beds were tested. The comparison of ethylene decomposition...
-
XPS-TiO2 heated in H2
Dane BadawczeThese XPS spectra were recorded for TiO2 heat-treated at 450-600oC in H2. Surface oxygen groups were determined. Deconvolution of Ti 2p peak allowed to determine Ti3+ on the titania surface.
-
TG analyses - content of SiO2 and TiO2 in polystyrene
Dane BadawczeTG analyses were performed for polystyrene spheres coating by SiO2 and then coating by SiO2-TiO2. Thermal analyses of polystyrene spheres only were also performed. The content of inorganic remaining was used for calculation the quantity of coating SiO2 and TiO2 in the polystyrene spheres.
-
Physicochemical and photocatalytic data of Cu-TiO2/Ti3C2 composites
Dane BadawczeIn this dataset, we include the data regarding the physicochemical properties (XRD, DR/UV-vis, photoluminescence, electrochemistry) and photocatalytic activity of TiO2/Ti3C2 and Cu-TiO2/Ti3C2 composites in the reaction of carbamazepine degradation. Herein we present the results for pure TiO2/Ti3C2 and composites modified with copper particles (0.25%,...
-
Ethylene decomposition on TiO2 under UV
Dane BadawczeData contain chromatograms recorded during decomposition of ethylene over TiO2 in a flow reactor under UV irradiation. Semilac UV lamp with total power of 72 W was used as a source of UV light. Chromatograms were recorded in Trace GC Ultra chromatograph equipped in FID detector. Sampling was realised via the dosing sample loop. TiO2 was coated on the...
-
SEM of TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeData contain some SEM images of TiO2 taken after its heat treatment in Ar or H2 at 400-600oC. Treated TiO2 was crystalline anatase phase with 3-4 % of rutile nclei.
-
EPR of TiO2 hydrogenated at 500 and 600oC
Dane BadawczeData contain EPR spectra of TiO2 (anatase phase) heat treated in H2 at 500 and 600oC. Sample heated at 500oC contained 4 wt% of rutile and that at 600oC 8 wt% of rutile.
-
FTIR-TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeData contain FTIR diffuse eflectance spectra of TiO2, which was heat-treated at 400-600oC in Ar or H2. Hydrogen reduced TiO2 revealed new bands due to the adsorption of some species on the titania oxygen vacancy sites.
-
X-ray diffraction (XRD) and particle size distribution (PSD) data of iron oxide (Fe3O4) - magnetite particles
Dane BadawczeDataset presenting X-ray diffractogram and particle size distribution of nanomagnetite (Fe3O4) iron oxide particles purchased from Sigma Aldrich (637106).X-ray diffraction study was performed with a PRO X-ray diffractometer (X’Pert PRO Philips diffractometer, Co. Ka radiation, Almelo, Holland), while PSD was determined using laser diffraction technique...
-
XRD-TiO2 heat-treated at 400-600oC in Ar or H2
Dane BadawczeThese data contain XRD patterns of TiO2 heat-treated at 400-600oC in Ar or H2. Two pases of TiO2 were identified: anatase and rutile.