THE EFFECT OF WET UNDERWATER WELDING ON COLD CRACKING SUSCEPTIBILITY OF DUPLEX STAINLESS STEEL
PublikacjaABSTRACT The present work was conducted to assess the weldability of duplex stainless steel in underwater conditions. Metal manual arc welding (MMA) with the use of coated electrodes was used in the investigations. Tekken weldability tests were performed underwater at 0.5 m depth and in the air. Nondestructive tests, metallographic examinations of welds, ferrite content assessment in microstructure and hardness test were performed....
-
APPLICATION POSSIBILITIES OF THE S960 STEEL IN UNDERWATER WELDED STRUCTURES
PublikacjaIn this paper, the application possibilities of the ultra-high strength (UHSS). Domex 960 steel in the underwater welded structures are analyzed. In the research, the investigated material has been tested in bead-on-plate wet welding conditions with the usage of different heat input values, namely 0.63 kJ/mm, 0.72 kJ/mm and 0.93 kJ/mm. Specimens were performed by the manual metal arc (MMA) welding method with the usage of rutile...
-
Spawalność ferrytyczno-austenitycznej stali odpornej na korozję typu dupleks 2205 w warunkach podwodnych
PublikacjaPraca dotyczy problemów spawalności stali odpornej na korozję typu dupleks w warunkach spawania mokrego elektrodami otulonymi i lokalną komorą suchą. Całość rozprawy składa się z dwóch części. Część pierwsza to przegląd literatury, w którym omówiono główne problemy wynikające z przeniesienia procesu spawania pod wodę oraz sposoby minimalizowania negatywnego wpływu środowiska. Część druga jest częścią doświadczalną, zawiera tezę...
-
Assessment of hydrogenation of deposited metal of P 62 MR covered electrodes
PublikacjaThe determination of diffusible hydrogen content in deposited metal of P 62 MR covered electrodes for manual metal arc welding by mercury method was carried out. The test results indicate that covered electrodes 62 P MR grade generate a mean of 4.02 ml/100g of diffusible hydrogen in deposited metal, which is consistent with H5 class.
-
Diffusible hydrogen content in deposited metal of multilayer welded joints
PublikacjaThe article describes manufacturing technology of multilayer joints in terms of control the diffusible hydrogen content. Diffusible hydrogen content in deposited metal for multilayer welded joints made of covered rutile electrodes or covered cellulosic and basic electrodes was determined. It was found that after four beads, the diffusible hydrogen content decreases in the case of the first technology from 36 ml/100 g to 18 ml/100...
-
Bead-on-Plate Underwater Wet Welding on S700MC Steel
PublikacjaThe participation of high strength steels in marine and offshore structures is increasing, which makes it necessary to develop recommendations for underwater repair welding works. The article presents the results of bead-on-plate welded specimens made of S700MC high strength steel in underwater wet welding conditions by covered elec- trodes. Three specimens with heat input values in the range 0.91-1.05 kJ/mm were made. The specimens...