Crack monitoring in concrete beams under bending using ultrasonic waves and coda wave interferometry: the effect of excitation frequency on coda
PublikacjaConcrete is one of the most widely used construction materials in the world. In recent years, various non-destructive testing (NDT) and structural health monitoring (SHM) techniques have been investigated to improve the safety and control of the current condition of concrete structures. This study focuses on micro-crack monitoring in concrete beams. The experimental analysis was carried out on concrete elements subjected to three-point...
-
Coda wave interferometry in monitoring the fracture process of concrete beams under bending test
PublikacjaEarly detection of damage is necessary for the safe and reliable use of civil engineering structures made of concrete. Recently, the identification of micro-cracks in concrete has become an area of growing interest, especially using wave-based techniques. In this paper, a non-destructive testing approach for the characterization of the fracture process was presented. Experimental tests were made on concrete beams subjected to mechanical...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #3)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #1)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #4)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Wave propagation signals in concrete beams under 3-point bending
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete beams with dimensions 40 x 40 x 160 cm3under the 3-point bending. The beams were made of concrete with the following ingredients: CEM I 42.5R (450 kg/m3), water (177 kg/m3), sand 0-2 (675 kg/m3) and gravel 2-8 (675 kg/m3). The bending test was performed using a Zwick/Roell Z10...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #2)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...